STP1546

    Estimation of Corrosion Fatigue-Crack Growth through Frequency Shedding Method

    Published: Jul 2012


      Format Pages Price  
    PDF Version (11M) 18 $25   ADD TO CART
    Complete Source PDF (114M) 18 $109   ADD TO CART


    Abstract

    Corrosion fatigue-crack growth characteristics are important for the design of marine and off-shore structures. Design of critical components requires data on fatigue-crack growth rate at very low frequencies of the order of 10−2 to 10−3 Hz. Experiments at low frequencies pose practical difficulties of enormous test duration. To address this, it is proposed to estimate corrosion crack growth characteristics using a frequency shedding method where the frequency is shed with crack advance using an exponential law. Fatigue-crack growth rate tests have been conducted on Ni–Mn–Cr steel at a constant ΔK range of 18 MP√m (lower Paris regime) under lab air conditions as well as 3.5 % NaCl solution. Crack growth rate data plotted as a function of test frequency presents a straight-line trend in log–log scale for a frequency range of 1–0.1 Hz; however, there is a change in trend when the frequencies are dropped further, which could be due to domination of corrosion mechanism. To understand the role of crack closure, crack closure estimates were obtained at periodic intervals of crack length and the effective stress intensity graphs suggest acceleration in crack growth rate due to corrosion as the frequency is reduced.

    Keywords:

    corrosion fatigue, frequency shedding, Ni–Mn–Cr steel, crack closure, lab air, 3.5 %, NaCl solution


    Author Information:

    Prakash, Raghu V.
    Dept. of Mechanical Engineering, Indian Institute of Technology Madras, Chennai

    Dhinakaran, Sampath
    Dept. of Mechanical Engineering, Indian Institute of Technology Madras, Chennai


    Paper ID: STP154620120009

    Committee/Subcommittee: E08.07

    DOI: 10.1520/STP154620120009


    CrossRef ASTM International is a member of CrossRef.