Chitosan/Graphene Oxide Nanocomposite Coatings on Magnesium Alloy: Corrosion and Biocompatibility Properties

CODEN: MPCACD

Abstract

In the present study, optimal conditions for the fabrication of chitosan (CS)/graphene oxide (GO) nanocomposite coatings were evaluated by the pulse electrodeposition (PED) process on Mg–2wt%Zn scaffolds. The size distribution of CS, GO suspension, and CS/GO composite was evaluated using dynamic light scattering. The coatings’ microstructure and morphologies were investigated by Fourier-transform infrared spectroscopy, ultraviolet-visible spectroscopy, Raman spectroscopy, thermogravimetric analysis, derivative thermogravimetric analysis, differential thermal analysis, and scanning electron microscopy. The Taguchi statistical method was used to optimize PED parameters, including peak current density (j), duty cycle, and GO nanosheets content (1, 2, and 3 percent by weight [wt%]). Results showed that optimal coatings were produced under the conditions of 2 wt% GO, j = 20 mA/cm2, duty cycle = 0.5, and pH = 5. The process’s time, temperature, and frequency were 20 min, 37°C, and 1,000 Hz. The biocompatibility of coatings was assessed by in vitro test. The results of cell viability and adhesion of MG63 cells on optimal coating are promising for application in bone tissue engineering.

Author Information

Montazeri, Arash
Department of Nanotechnology, Faculty of Engineering, University of Guilan, Rasht, Iran
Ranjbar Hamghavandi, Mohammad
Department of Nanotechnology, Faculty of Engineering, University of Guilan, Rasht, Iran
Sadat Nezhadfard, Mahla
Chemical Engineering, Faculty of Engineering, University of Guilan, Rasht, Iran
Yeganeh Kari, Ali
Chemical Engineering, Faculty of Engineering, University of Guilan, Rasht, Iran
Pages: 18
Price: $25.00
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Stock #: MPC20220106
ISSN: 2379-1365
DOI: 10.1520/MPC20220106