Mechanism-Based Variability in Fatigue Life of Ti-6Al-2Sn-4Zr-6Mo

CODEN: JAIOAD

Abstract

The variability in fatigue life of a Ti-6Al-2Sn-4Zr-6Mo alloy was studied. The cumulative life distribution plot was found to be composed of two distinct failure mechanisms, designated as Type-I and Type-II. The likelihood of Type-I vs. Type-II failure shifted with respect to the stress level, such that at lower stress levels, there was increased probability of Type-II failure. It also was found that the variability in life was introduced primarily at the crack nucleation stage, specifically, formation of a stage-I crack across an equiaxed primary-α particle.

Author Information

Jha, SK
Systran Federal Corporation, Dayton, OH
Larsen, JM
Air Force Research Laboratory, Materials and Manufacturing Directorate, AFRL/MLLMN, Wright Patterson AFB, Dayton, OH
Rosenberger, AH
Air Force Research Laboratory, Materials and Manufacturing Directorate, AFRL/MLLMN, Wright Patterson AFB, Dayton, OH
Hartman, GA
The University of Dayton Research Institute, Dayton, OH
Pages: 12
Price: $25.00
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Stock #: JAI11570
ISSN: 1546-962X
DOI: 10.1520/JAI11570