D543-21 Standard Practices for Evaluating the Resistance of Plastics to Chemical Reagents
-See also WK96332 proposed Revision
D570-22 Standard Test Method for Water Absorption of Plastics
D1042-22 Standard Test Method for Linear Dimensional Changes of Plastics Caused by Exposure to Heat and Moisture
D1435-20 Standard Practice for Outdoor Weathering of Plastics
D1499-13(2021) Standard Practice for Filtered Open-Flame Carbon-Arc Exposures of Plastics
D1712-09(2020) Standard Practice for Resistance of Plastics to Sulfide Staining
D6360-15(2021) Standard Practice for Enclosed Carbon-Arc Exposures of Plastics
D3045-18 Standard Practice for Heat Aging of Plastics Without Load
-See also WK90246 proposed Revision
D4459-21 Standard Practice for Xenon-Arc Exposure of Plastics Intended for Indoor Applications
D618-21 Standard Practice for Conditioning Plastics for Testing
-See also WK94270 proposed Revision
D2565-23 Standard Practice for Xenon-Arc Exposure of Plastics Intended for Outdoor Applications
D4329-21 Standard Practice for Fluorescent Ultraviolet (UV) Lamp Apparatus Exposure of Plastics
-See also WK95819 proposed Revision
D4364-13(2022)e1 Standard Practice for Performing Outdoor Accelerated Weathering Tests of Plastics Using Concentrated Sunlight
D4674-19 Standard Practice for Accelerated Testing for Color Stability of Plastics Exposed to Indoor Office Environments
-See also WK78769 proposed Revision
D5071-06(2021) Standard Practice for Exposure of Photodegradable Plastics in a Xenon Arc Apparatus
D5208-14(2022) Standard Practice for Fluorescent Ultraviolet (UV) Exposure of Photodegradable Plastics
-See also WK81670 proposed Reapproval with Editorial Change
D5272-08(2021) Standard Practice for Outdoor Exposure Testing of Photodegradable Plastics
D5870-22 Standard Practice for Calculating Property Retention Index of Plastics

D756-93 Practice for Determination of Weight and Shape Changes of Plastics Under Accelerated Service Conditions (Withdrawn 1998)