Effects of Composition, Microstructure, and Temperature on Irradiation Hardening of Pressure Vessel Steels

Source

As part of an overall effort to determine the fundamental mechanisms of neutron irradiation embrittlement of pressure vessel steels, four commercial alloys (two welds and two plates) and eight model alloys have been irradiated to a fluence of ~7 × 1018 neutrons (n)/cm2 (E > 1 MeV) at a flux of ~3 × 1012 n/cm2 · s and at four temperatures from 270°C to 315°C. The alloys had a range of copper and nickel concentrations and microstructures. Post-irradiation microhardness testing showed the following: radiation hardening systematically decreased, albeit modestly, with increasing irradiation temperature; radiation hardening increased nonlinearily with copper concentration, with decreasing incremental effect at high levels; radiation hardening was not influenced by nickel but was sensitive to microstructure. These results were found to be broadly consistent with a physically-based model in which the hardening is primarily due to an irradiation-enhanced copper precipitation with a secondary contribution from radiation-induced defect cluster formation.

Author Information

Lucas, Glenn, E.
Department of Chemical and Nuclear Engineering, University of California, Santa Barbara, Santa Barbara, CA, US
Odette, G., Robert
Department of Chemical and Nuclear Engineering, University of California, Santa Barbara, Santa Barbara, CA, US
Lombrozo, Peter M.
Department of Chemical and Nuclear Engineering, University of California, Santa Barbara, Santa Barbara, CA, US
Sheckherd, J., William
Department of Chemical and Nuclear Engineering, University of California, Santa Barbara, Santa Barbara, CA, US
Price: $25.00
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Developed by Committee: E10
Pages: 900–930
DOI: 10.1520/STP87019850023
ISBN-EB: 978-0-8031-7679-9
ISBN-13: 978-0-8031-0592-8