Tensile and Fracture Behavior of a Nitrogen-Strengthened, Chromium-Nickel-Manganese Stainless Steel at Cryogenic Temperatures

Source

J-integral fracture and conventional tensile properties are reported for an electroslag remelted Fe-21Cr-6Ni-9Mn austenitic stainless steel that contains 0.28 percent nitrogen as an interstitial strengthening element. Results at room (295 K), liquid-nitrogen (76 K), and liquid-helium (4 K) temperatures demonstrated that the yield strength and fracture toughness of this alloy are inversely related and strongly temperature dependent. Over the investigated temperature range, the yield strength tripled to 1.24 GPa (180 ksi) at 4 K. The fracture toughness, as measured using 3.8-cm-thick (1.5 in.) compact specimens, decreased considerably between 295 and 4 K. During plastic deformation at 295 K the alloy undergoes slight martensitic transformation, but at 76 and 4 K it transforms extensively to martensites. The amount of body-centered cubic (bcc) martensite formed during tension tests was measured as a function of elongation.

Author Information

Tobler, RL
Institute for Basic Standards, National Bureau of Standards, Boulder, Colo.
Reed, RP
Institute for Basic Standards, National Bureau of Standards, Boulder, Colo.
Price: $25.00
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Developed by Committee: E08
Pages: 537–552
DOI: 10.1520/STP35847S
ISBN-EB: 978-0-8031-4739-3
ISBN-13: 978-0-8031-0330-6