Texture Strengthening and Fracture Toughness of Titanium Alloy Sheet at Room and Cryogenic Temperatures

Source

Biaxial yield strengths as high as 1.53 times uniaxial yield strength were obtained from burst tests of 6-in.-diameter cylindrical pressure vessels (1 to 2 stress field) fabricated from two textured titanium alloys, Ti-4Al-0.2O and Ti-5Al-2.5Sn ELI. Material nominally 0.020 in. thick was tested at 70, -320, and -423 F. While the Ti-4Al-0.2O alloy generally had superior biaxial smooth properties at the three test temperatures, the Ti-5Al-2.5Sn ELI alloy exhibited less notch sensitivity at-320 and -423 F. It is demonstrated that plastic Poisson's ratio obtained from a uniaxial test could be used to characterize the degree of texture in the two alloys and provide a means for predicting biaxial strengthening.

Author Information

Sullivan, TL
Lewis Research Center, National Aeronautics and Space Administration, Cleveland, Ohio
Price: $25.00
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Developed by Committee: B10
Pages: 236–247
DOI: 10.1520/STP33629S
ISBN-EB: 978-0-8031-4571-9
ISBN-13: 978-0-8031-0748-9