Prediction of Crack Growth Under Creep-Fatigue Loading Conditions

Source

Crack growth data are presented on a brittle and a ductile low alloy steel and a nickel base superalloy which have been subjected to combined static and cyclic loading at elevated temperatures. The cyclic tests have been conducted between fixed load and fixed displacement ranges. Distinct regions of fatigue and creep dominated cracking have been identified. It is shown that crack growth eventually ceases because of load relaxation in the constant displacement amplitude tests. Fracture of a component made of the ductile steel is unlikely to occur under this type of low-cycle fatigue loading, but significant cracking is possible with the brittle steel. Where cyclic crack growth is creep controlled, it is shown that crack propagation rates can be predicted from static creep data using the creep fracture mechanics parameter C*.

Author Information

Nikbin, KM
Imperial College, London, England
Webster, GA
Imperial College, London, England
Price: $25.00
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Developed by Committee: E08
Pages: 281–292
DOI: 10.1520/STP24487S
ISBN-EB: 978-0-8031-5035-5
ISBN-13: 978-0-8031-0944-5