The Impact of Curing Conditions on the Appearance of Sealant Before and After Artificial Weathering

Source

This paper presents our preliminary laboratory research to determine the effects of various moisture and temperature conditions during cure, and joint extension after cure, on the internal and external appearance of a two-part polyurethane sealant before and after artificial weathering. We examined the impact of these conditions on the development of voids within the sealant, softening or tackiness on the sealant, and crazing and splitting at the sealant surface. Improper mixing created most of the large internal voids. Application of sealant on a damp substrate produced foaming in the sealant at the bond surface. Contact with water during cure softened the sealant surface, but not the entire thickness of the sealant. Artificial weathering caused surface crazing, but combining artificial weathering and constant extension produced deep cracks and splits through the sealant, with the depth of cracking increasing with greater extension. We performed additional testing on other sealants, including some that are not two-part polyurethane, by artificially weathering them at a constant extension. The crazing and splitting with these other sealants varied with the particular brand of sealant from no crazing to through-splits.

Author Information

Myers, JC
Simpson Gumpertz & Heger Inc., Consulting Engineers, Arlington, MA
Nelson, PE
Simpson Gumpertz & Heger Inc., Consulting Engineers, Arlington, MA
Price: $25.00
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Developed by Committee: C24
Pages: 9–21
DOI: 10.1520/STP24231S
ISBN-EB: 978-0-8031-5217-5
ISBN-13: 978-0-8031-1482-1