Challenging Embrittlement Trend Curves with Lower-Than-Usual Irradiation Temperature Data

Source

A series of irradiation-induced embrittlement trend curves was developed in the last decades and gathered in an Excel spreadsheet called PLOTTER to compare the various predicted values with the experimental data. A number of reactor pressure vessel materials, including forgings, plates, and welds with a variety of chemical compositions, were irradiated in the BR2 reactor to a neutron fluence ranging from ∼3 to ∼9 × 1019 n/cm², E >1 MeV at lower-than-usual irradiation temperatures (∼100 and 150°C) complemented with medium- to high-temperature irradiation data (260, 290, and 305°C) for comparison. Charpy impact tests were performed to determine the ductile-to-brittle transition temperature and the upper-shelf energy level. In addition, some tensile tests were also performed to determine the irradiation-induced hardening. Test results in terms of irradiation-induced hardening and embrittlement were determined and compared with the different embrittlement trend curve predictions. The results are discussed in the perspective of assessing the performances of the various embrittlement trend curves.

Author Information

Chaouadi, Rachid
SCK CEN, BE
Uytdenhouwen, Inge
SCK CEN, BE
Puzzolante, Jean-Louis
SCK CEN, BE
Price: $25.00
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Pages: 284–320
DOI: 10.1520/STP164720220046
ISBN-EB: 978-0-8031-7742-0
ISBN-13: 978-0-8031-7741-3