Test-Reactor Study of the Effect of Zirconia Coating of Inconel Spacer Cells on Shadow Corrosion

Source

Enhanced corrosion on zirconium-base alloys in proximity to other metals, the shadow effect, has been observed since the 1960s. Possible remedies against shadow corrosion have been investigated. The effect of 0.1- to 9-μm-thick zirconia (ZrO2) coatings of Inconel X-750 spacer cells on shadow corrosion of fully recrystallized LK3 Zircaloy-2 boiling water reactor cladding is investigated in this paper. The coatings were produced by a combination of two solution-based techniques, where (i) a nanoparticle-based route was used to build thick coatings, and (ii) a modified alkoxide route was used to build thinner dense coatings. Twenty-one spacer cells, sixteen with ZrO2 coating and five uncoated reference spacer cells, were inserted along the central instrumentation tube in an instrumented fuel assembly in a boiling water reactor loop in the Halden test reactor. The instrumented fuel assembly was subsequently operated at high power for 149 days. The investigations revealed that shadow corrosion occurred on the Zircaloy-2 tubing under all spacer cells. The significance of the shadow was strongly affected by the thickness of the ZrO2 coating from the spacer cells. Small effects were observed for coating thicknesses below 2.5 μm, while thicknesses of 4.5 and 9 μm reduced the shadow corrosion up to 42 and 26%, respectively.

Author Information

Anghel, Clara
Fuel Materials Center of Excellence, Västerås, SE
Limbäck, Magnus
Fuel Materials Center of Excellence, Västerås, SE
Westin, Gunnar
Dept. of Chemistry, Ångström Laboratory, Uppsala University, Uppsala, SE
Tverberg, Terje
Institute for Energy Technology, Halden, NO
Andersson, Björn
Fuel Materials Center of Excellence, Västerås, SE
Leideborg, Michael
Dept. of Chemistry, Ångström Laboratory, Uppsala University, Uppsala, SE
Wright, Jonathan
Fuel Materials Center of Excellence, Västerås, SE
Price: $25.00
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Pages: 343–364
DOI: 10.1520/STP162220190032
ISBN-EB: 978-0-8031-7691-1
ISBN-13: 978-0-8031-7690-4