Fretting Corrosion Mechanisms at Modular Implant Interfaces


Modular connections have been commonly and successfully utilized in orthopaedic implant systems for the last 15 or so years, particularly at the head/neck junction in total hip arthroplasty (THA). However, recent retrieval studies have shown that some of the tapered junctions between femoral heads and stems in total hip arthoplasty can be prone to fretting corrosion, and may be a cause for concern in the longevity of implants. Fretting corrosion, which may release metallic products (particulate debris and ions) into the joint space, is a complex phenomenon in which the interplay between mechanically induced interfacial micromotion (fretting) and electrochemical corrosive activity play an important role, along with materials selection and processes. This suggests that interfacial fretting corrosion at modular implant interfaces can be significantly affected by the design variables of the modular junction. The working hypothesis of this study was that different designs of the modular head/stem combination of femoral hip prostheses exhibit different release of fretting corrosion metal products during fatigue testing used to simulate ten years of in vivo service. Three designs of femoral head (Co-Cr-Mo alloy) and stem (Ti-6Al-4V alloy) combinations were investigated in this study. The study included detailed taper metrology followed by environmental fatigue testing of the tapered junctions. The results of this study showed that important taper design differences do exist in the three constructs tested, and these differences manifested in different fretting corrosion behavior.

Author Information

Jani, SC
Smith and Nephew Richards, Inc., Memphis, TN
Sauer, WL
Smith and Nephew Richards, Inc., Memphis, TN
McLean, TW
Smith and Nephew Richards, Inc., Memphis, TN
Lambert, RD
Smith and Nephew Richards, Inc., Memphis, TN
Kovacs, P
Smith and Nephew Richards, Inc., Memphis, TN
Price: $25.00
Contact Sales
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Developed by Committee: F04
Pages: 211–225
DOI: 10.1520/STP12034S
ISBN-EB: 978-0-8031-5359-2
ISBN-13: 978-0-8031-2415-8