Corrosion Behavior of Surface Nanostructured IN718 Superalloy at 650°C

CODEN: MPCACD

Abstract

In the present study, the process of ultrasonic shot peening (USP) was adopted for developing nanostructures with a grain size of 62 ± 10 nm on the surface of the alloy IN718. The effect of nanostructures was investigated on high-temperature corrosion behavior under cyclic exposure at 650°C for 100 h in different salty environments (weight percent): 100NaCl (T1), 75Na2SO4 + 25NaCl (T2), and 90Na2SO4 + 5NaCl + 5V2O5 (T3). A near parabolic rate law was observed in both non-treated and treated conditions; however, the parabolic rate constant (kp) was reduced for the USP-treated specimens coated with Salt T1 and Salt Mixtures T2 and T3 by nearly 41 %, 52 %, and 50 %, respectively, with respect to the non-treated specimens. Several oxides and spinels such as TiO2, Fe2O3, Fe3O4, Cr2O3, FeVO4, NbO2, NiFe2O4, NiCr2O4, NiVO3, FeNbO4, FeCr2O4, Na2Cr2O7, and Cr2(MoO4)3 and sulfides NiS and FeS and chlorides CrCl3 and NiCl2 were observed in both treated as well as non-treated samples.

Author Information

Kumar, Sanjeev
DRDO Defence Metallurgical Research Laboratory, DMRL Hyderabad Kanchanbagh, Hyderabad, Telangana, India
Chattopadhyay, K.
Department of Metallurgical Engineering, Indian Institute of Technology (Banaras Hindu University), Varanasi, Uttar Pradesh, India
Alam, Z.
DRDO Defence Metallurgical Research Laboratory, DMRL Hyderabad Kanchanbagh, Hyderabad, Telangana, India
Singh, Vakil
Department of Metallurgical Engineering, Indian Institute of Technology (Banaras Hindu University), Varanasi, Uttar Pradesh, India
Satyanarayana, D. V. V.
DRDO Defence Metallurgical Research Laboratory, DMRL Hyderabad Kanchanbagh, Hyderabad, Telangana, India
Kumar, Vikas
DRDO Defence Metallurgical Research Laboratory, DMRL Hyderabad Kanchanbagh, Hyderabad, Telangana, India
Pages: 14
Price: $25.00
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Stock #: MPC20200156
ISSN: 2379-1365
DOI: 10.1520/MPC20200156