Microstructure, Hardness, Wear, and Magnetic Properties of (Tantalum, Niobium) Carbide-Nickel–Sintered Composites Fabricated from Blended and Coated Particles

CODEN: MPCACD

Abstract

(Tantalum, niobium) carbide-nickel composites were prepared by the powder metallurgy technique. Microsize (tantalum, niobium) carbide particles were reinforced in the nickel matrix. Different nickel contents were added to (tantalum, niobium) carbide powders by two different methods, namely, blending and electroless coating. The results of the microstructure show a good distribution of the (tantalum, niobium) carbide particles in the nickel matrix. The produced (tantalum, niobium) carbide-nickel composite powders were cold compacted at 400 MPa and sintered under vacuum at 1,450°C for 90 min. The density of the (tantalum, niobium) carbide-nickel–sintered materials was measured by the Archimedes method. The mechanical properties of the obtained sintered materials were evaluated by measuring the Vickers hardness and the wear rate using a pin-on-ring wear test machine. The microstructure of the sintered (tantalum, niobium) carbide-nickel as well as the microstructure of worn samples were investigated by a scanning electron microscope. The results revealed that the (tantalum, niobium) carbide-nickel–sintered materials, which were prepared by the electroless nickel coating of (tantalum, niobium) carbide particles, have a homogeneous microstructure and exhibit higher relative density, hardness, and low specific wear rate than the samples of the (tantalum, niobium) carbide/nickel–sintered materials prepared by blending of nickel with the (tantalum, niobium) carbide powders. The magnetic properties of the obtained blended and coated (tantalum, niobium) carbide particles as well as the sintered one have been studied. It was observed that the saturation magnetization is increased by increasing the nickel content.

Author Information

Yehia, Hossam M.
Department of Production Technology, Faculty of Technology and Education, Helwan University, Cairo, Egypt
Daoush, Walid M.
Department of Production Technology, Faculty of Technology and Education, Helwan University, Cairo, Egypt Department of Chemistry, College of Science, Imam Mohammad Ibn Saud Islamic University (IMSIU), Riyadh, KSA
Abdel Mouez, F.
Central Metallurgical Research and Development Institute, Cairo, Helwan, Egypt
El-Sayed, Mohamed H.
Central Metallurgical Research and Development Institute, Cairo, Helwan, Egypt Department of Mechanical Engineering, Jouf University, Sakakka, Al-Jouf, KSA
El-Nikhaily, Ahmed E.
Mechanical Department, Faculty of Technology and Education, Suez University, Suez, Egypt
Pages: 13
Price: $25.00
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Stock #: MPC20190128
ISSN: 2379-1365
DOI: 10.1520/MPC20190128