Significance and Use
4.1 Although there are ASTM test methods for exfoliation testing, they concentrate on specific procedures for test methodology itself. Existent test methods do not discuss material variables that can affect performance. Likewise they do not address the need to establish the suitability of an accelerated test for alloys never previously tested nor the need to correlate results of accelerated tests with tests in outdoor atmospheres and with end-use performance.
4.2 This guide is a compilation of the experience of investigators skilled in the art of conducting exfoliation tests and assessing the degree and significance of the damage encountered. The focus is on two general aspects: guides to techniques that will enhance the likelihood of obtaining reliable information, and tips and procedures to avoid pitfalls that could lead to erroneous results and conclusions.
4.3 The following three areas of testing are considered: the test materials starting with the “as-received” sample up through final specimen preparation, the corrosion test procedures including choice of test, inspection periods, termination point, and rating procedures, and analyses of results and methods for reporting them.
4.4 This guide is not intended as a specific corrosion test procedure by which to evaluate the resistance to exfoliation of an aluminum alloy product.
4.5 This guide is not intended as a basis for specifications, nor as a guide for material lot acceptance.
1.1 This guide differs from the usual ASTM standard in that it does not address a specific test. Rather, it is an introductory guide for new users of various standard exfoliation test methods with consideration for specific aluminum alloy families (see Terminology for definition of exfoliation).
1.2 This guide covers aspects of specimen preparation, exposure, inspection, and evaluation for conducting exfoliation tests on aluminum alloys in both laboratory accelerated environments and in natural, outdoor atmospheres. The intent is to clarify any gaps in existent test methods.
1.3 The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.