Damage Processes in a Quasi-Isotropic Composite Short Beam Under Three-Point Loading



Composite materials have complex failure modes that include delamination, fiber debonding and breakage, and matrix microcracking. In this paper, the influence of these damage modes on the failure of the short-beam three-point bend test is investigated for a composite with a quasi-isotropic layup. Failure is found to initiate in a region near the point of application of the load, a location where classical-type analytical descriptions of specimen behavior are unreliable. Furthermore, the locations of failure show little reproducibility. Observed fracture behavior is explained in terms of the overall stress state in the beam before fracture, and failure is predicted from the stress map, using the maximum strain criterion.

Author Information

Fortson, BH
Space Kinetic Impact and Debris Branch, Phillips Laboratory, Kirktland Air Force Base, NM
Armanios, EA
School of Aerospace Engineering, Georgia Institute of Technology, Atlanta, GA
Pages: 8
Price: $25.00
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Stock #: CTR10233J
ISSN: 0884-6804
DOI: 10.1520/CTR10233J