ASTM C1368-10

Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Strength Testing at Ambient Temperature

Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Strength Testing at Ambient Temperature C1368-10 ASTM|C1368-10|en-US Standard Test Method for Determination of Slow Crack Growth Parameters of Advanced Ceramics by Constant Stress-Rate Strength Testing at Ambient Temperature Standard new BOS Vol. 15.01 Committee C28
$ 83.00 In stock

Significance and Use

For many structural ceramic components in service, their use is often limited by lifetimes that are controlled by a process of SCG. This test method provides the empirical parameters for appraising the relative SCG susceptibility of ceramic materials under specified environments. Furthermore, this test method may establish the influences of processing variables and composition on SCG as well as on strength behavior of newly developed or existing materials, thus allowing tailoring and optimizing material processing for further modification. In summary this test method may be used for material development, quality control, characterization, and limited design data generation purposes. The conventional analysis of constant stress-rate testing is based on a number of critical assumptions, the most important of which are listed in the next paragraphs.

The flexural stress computation for the rectangular beam test specimens or the equibiaxial disk flexure test specimens is based on simple beam theory, with the assumptions that the material is isotropic and homogeneous, the moduli of elasticity in tension and compression are identical, and the material is linearly elastic. The average grain size should be no greater than one fiftieth of the beam thickness.

Scope

1.1 This test method covers the determination of slow crack growth (SCG) parameters of advanced ceramics by using constant stress-rate rectangular beam flexural testing, or ring-on-ring biaxial disk flexural testing, or direct tensile strength, in which strength is determined as a function of applied stress rate in a given environment at ambient temperature. The strength degradation exhibited with decreasing applied stress rate in a specified environment is the basis of this test method which enables the evaluation of slow crack growth parameters of a material.

Note 1—This test method is frequently referred to as dynamic fatigue testing (Refs (1-3) ) in which the term fatigue is used interchangeably with the term slow crack growth. To avoid possible confusion with the fatigue phenomenon of a material which occurs exclusively under cyclic loading, as defined in Terminology E1823, this test method uses the term constant stress-rate testing rather than dynamic fatigue testing.

Note 2—In glass and ceramics technology, static tests of considerable duration are called static fatigue tests, a type of test designated as stress-rupture (See Terminology E1823).

1.2 Values expressed in this test method are in accordance with the International System of Units (SI) and .

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Price:
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Book of Standards Volume: 15.01
Developed by Subcommittee: C28.01
Pages: 11
DOI: 10.1520/C1368-10
ICS Code: 81.060.30