ASTM B619-10e1

Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe

Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe B0619-10E01 ASTM|B0619-10E01|en-US Standard Specification for Welded Nickel and Nickel-Cobalt Alloy Pipe Standard new BOS Vol. 02.04 Committee B02
$ 75.00 In stock

Abstract

This specification covers welded pipe of nickel and nickel-cobalt alloys (UNS N10001; UNS N10242; UNS N10665; UNS N12160; UNS N10624; UNS N10629; UNS N10675; UNS N10276; UNS N06455; UNS N06007; UNS N06975; UNS N08320; UNS 06002; UNS N06022; UNS N06035; UNS N06058; UNS N06059; UNS N06200; UNS N06985; UNS N06030; UNS R30556; UNS N08031; UNS N06230; UNS N06686; UNS N06210; and UNS R20033). Two classes of pipe are covered as Class I which is as welded and solution annealed or welded and sized and solution annealed; and Class II which is welded, cold worked, and solution annealed. All pipes shall be furnished in the solution annealed and descaled condition. The pipe shall be made from flat-rolled alloy by an automatic welding process with no addition of filler metal. Subsequent to welding and prior to final heat treatment, Class II pipes shall be cold worked either in both weld and base metal or in weld metal only. The material shall conform to the composition limits set by this specification. Tensile strength, yield strength and elongation of the material shall conform to the mechanical requirements. Tension test, flattening test, transverse guided bend test, and hydrostatic or nondestructive electric test shall be performed.

Scope

1.1 This specification covers welded pipe of nickel and nickel-cobalt alloys (UNS N10001; UNS N10242; UNS N10665; UNS N12160; UNS N10624; UNS N10629; UNS N10675; UNS N10276; UNS N06455; UNS N06007; UNS N06975; UNS N08320; UNS N06002; UNS N06022; UNS N06035; UNS N06058; UNS N06059; UNS N06200; UNS N10362; UNS N06985; UNS N06030; UNS R30556; UNS N08031; UNS N06230; UNS N06686; UNS N06210; and UNS R20033) as shown in Table 1.

1.2 This specification covers pipe in Schedules 5S, 10S, 40S, and 80S through 8-in. nominal pipe size and larger as set forth in ANSI B36.19 (see Table 2).

1.3 Two classes of pipe are covered as follows:

1.3.1 Class IAs welded and solution annealed or welded and sized and solution annealed.

1.3.2 Class IIWelded, cold worked, and solution annealed.

1.4 All pipe shall be furnished in the solution annealed and descaled condition. When atmosphere control is used, descaling is not necessary.

1.5 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

TABLE 1 Chemical Requirements

Composition Limits, %
NiCrMo FeWCSi
max
Co MnVP
max
S
max
Ti CuCb
(Nb)
+Ta
Al ZrLaNBCb
(Nb)
TaNi+
Mo
Mg
Ni-Mo Alloys
N10001remainderA 1.0 max26.0- 30.04.0-6.0...0.05 max1.0 2.5 max1.0 max0.2- 0.40.040.03... ......
N10665remainderA 1.0 max26.0- 30.02.0 max...0.02 max0.10 1.0 max1.0 max... 0.040.03.........
N1067565.0 min1.0- 3.027.0- 32.01.0-3.03.0 max0.01 max0.103.0 max3.0 max0.20 max0.0300.010 0.20 max0.20 max... 0.50 max0.10 max... ......0.20 max0.20 max94.0- 98.0
N10629remainderA0.5- 1.526.0- 30.01.0-6.0...0.01 max0.052.5 max1.5 max...0.040.01 ...0.5 max...0.1- 0.5............ .........
N10624remainderA 6.0- 10.021.0- 25.05.0-8.0...0.01 max0.10 1.0 max1.0 max... 0.0250.01...0.5 max... ............... .........
Ni-Mo-Cr-Fe Alloy
N10242remainderA7.0- 9.024.0- 26.02.0 max0.03 max0.801.00 max0.80 max0.0300.0150.50 max0.50 max0.006 max
Low C Ni-Cr-Mo Alloys
N10276remainderA 14.5- 16.515.0- 17.04.0-7.03.0- 4.50.010 max0.08 2.5 max1.0 max0.35 max 0.040.03.........
N06022remainderA 20.0- 22.512.5- 14.52.0-6.02.5- 3.50.015 max0.08 2.5 max0.5 max0.35 max0.020.02... ......
N06035remainderA32.25-
34.25
7.60-
9.00
2.00 max0.60 max0.050 max0.601.00 max0.50 max0.20 max0.0300.015...0.30 max...0.40 max
N06455remainderA 14.0- 18.014.0- 17.03.0 max...0.015 max0.08 2.0 max1.0 max... 0.040.030.70 max......
Ni-Cr-Fe-Mo-Cu Alloys
N06007remainderA 21.0- 23.55.5- 7.518.0-21.0 1.0 max0.05 max1.0 2.5 max1.0- 2.0... 0.040.03...1.5- 2.51.75- 2.5
N0697547.0-52.023.0- 26.05.0- 7.0remainder... 0.03 max1.0...1.0 max... 0.030.030.70- 1.500.70- 1.20...
N06985remainderA 21.0- 23.56.0- 8.018.0-21.0 1.5 max0.015 max1.0 max 5.0 max1.0 max... 0.040.03...1.5- 2.50.50 max
N06030remainderA 28.0- 31.54.0-6.013.0-17.0 1.5- 4.00.03 max0.8 5.0 max1.5 max... 0.040.02...1.0- 2.40.30- 1.50
Ni-Fe-Cr-Mo Alloys
N0832025.0-27.021.0- 23.04.0- 6.0remainder ...0.05 max1.0...2.5 max ...0.040.034xC min... ...
Ni-Cr-Mo-Fe Alloy
N06002 remainderA20.5- 23.08.0- 10.017.0-20.00.20- 1.00.05- 0.151.00.5-2.51.0 max...0.040.03 .........
Ni-Fe-Cr-Co Alloy
R3055619.0-22.521.0- 23.02.5- 4.0remainder 2.0- 3.50.05- 0.150.20- 0.8016.0- 21.00.50- 2.00...0.040.015... ......0.10- 0.500.001- 0.100.005- 0.100.10- 0.300.02 max0.30 max0.3- 1.25
Ni-Cr-W-Mo Alloy
N06230remainderA 20.0- 24.01.0- 3.03.0 max 13.0- 15.00.05- 0.150.25- 0.755.0 max0.30- 1.00...0.030.015... ......0.50 max...0.005- 0.050...0.015 max......
Low C-Ni-Cr-Mo Alloy
N06058balance20.0- 23.019.0- 21.01.5 max0.3 max0.010 max0.10 max0.3 max0.50 max0.0150.010...0.50 max...0.40 max0.02- 0.15
N06059balance22.0- 24.015.0- 16.51.5 max...0.010 max0.100.3 max0.5 max...0.0150.010...0.50 max...0.1- 0.4... ............... ...
Low C-Ni-Cr-Mo-Cu Alloy
N06200remainderA 22.0- 24.015.0- 17.03.0 max...0.010 max0.08 2.0 max0.50 max... 0.0250.010...1.3- 1.9... 0.50 max
Low-C-Ni-Mo-Cr Alloy
N10362remainderA13.8-
15.6
21.5-
23.0
1.25 max...0.010 max0.08...0.60 max...0.0250.010.........0.50 max........................
Low C-Ni-Fe-Cr-Mo-Cu Alloy
N0803130.0-32.026.0- 28.06.0- 7.0balance...0.015 max0.3...2.0 max ...0.0200.010...1.0- 1.4 ............0.15- 0.25 .........
Low C-Ni-Cr-Mo-W Alloy
N06686remainderA 19.0- 23.015.0- 17.05.0 max3.0- 4.40.010 max0.08 ...0.75 max...0.040.020.02- 0.25............ ...............
Ni-Co-Cr-Si Alloy
N12160remainderA 26.0- 30.01.0 max3.5 max 1.0 max0.15 max2.4- 3.027.0- 33.01.5 max...0.0300.0150.20- 0.80 ............... ......1.0 max...... ...
Cr-Ni-Fe-N Alloy
R2003330.0-33.031.0- 35.00.50- 2.0balance...0.015 max0.050...2.0 max ...0.020.01...0.3- 1.20 ............0.35- 0.60 ...............
Low C-Ni-Mo-Cr-Ta Alloy
N06210remainderA 18.0- 20.018.0- 20.01.0 max...0.015 max0.08 1.0 max0.50.35 max0.020.02 .................. ...1.5-
2.2
Editorially corrected.

A The composition of the remainder shall be determined arithmetically by difference.

TABLE 2 Dimensions of Welded Pipe

Note 1—The following table is a partial reprint of Table 1 of ANSI B36.19.

Note 2—The decimal thickness listed for the respective pipe sizes represents their nominal or average wall dimensions.

Nominal Pipe Size, Outside Diameter Nominal Wall Thickness
Schedule 5SA Schedule 10SASchedule 40SSchedule 80S
in.in.mmin. mmin.mmin.mm in.mm
1/80.40510.29 ......0.0491.240.068 1.73
¼0.54013.72 ......0.0651.650.088 2.24
3/80.67517.15 ......0.0651.650.091 2.31
½0.84021.34 0.0651.650.0832.110.109 2.77
¾1.05026.67 0.0651.650.0832.110.113 2.87
1.01.31533.410.065 1.650.1092.770.1333.38
1¼1.66042.16 0.0651.650.1092.770.140 3.56
1½1.90048.26 0.0651.650.1092.770.145 3.68
22.37560.330.065 1.650.1092.770.1543.91 0.2185.54
2½2.87573.03 0.0832.110.1203.050.203 5.160.2767.01
33.50088.900.083 2.110.1203.050.2165.33
3½4.000101.60 0.0832.110.1203.050.226 5.74
44.500114.300.083 2.110.1203.050.2376.02
55.563141.300.109 2.770.1343.400.2586.55
66.625168.280.109 2.770.1343.400.2807.11
88.625219.180.109 2.770.1483.760.3228.18

A Schedules 5S and 10S wall thicknesses do not permit threading in accordance with ANSI B2.1-1960.

Price:
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Book of Standards Volume: 02.04
Developed by Subcommittee: B02.07
Pages: 6
DOI: 10.1520/B0619-10E01
ICS Code: 23.040.15