ASTM B86-13

Standard Specification for Zinc and Zinc-Aluminum (ZA) Alloy Foundry and Die Castings

Standard Specification for Zinc and Zinc-Aluminum (ZA) Alloy Foundry and Die Castings B0086-13 ASTM|B0086-13|en-US Standard Specification for Zinc and Zinc-Aluminum (ZA) Alloy Foundry and Die Castings Standard new BOS Vol. 02.04 Committee B02
$ 75.00 In stock

Abstract

This specification covers commercial zinc, zinc-aluminum castings and continuous cast bar stock. Seven alloy compositions are specified and designated: Alloy 3; Alloy 7; Alloy 5; Alloy 2; ZA-8; ZA-12; ZA-27. The metal used in the manufacture of die castings shall be zinc alloy of a specified chemical composition conforming to the requirements specified. Impact test and tension test shall be made to conform to the specified requirements.

Scope

1.1 This specification covers commercial zinc, zinc-aluminum castings and continuous cast bar stock, as designated and specified in Table 1. Seven alloy compositions are specified and designated as follows:

Common

Traditional

ASTM A

UNS

 

 

 

 

Alloy 3

Zamak 3

AG 40A B

Z33525

Alloy 7

Zamak 7

AG 40B

Z33527

Alloy 5

Zamak 5

AC 41A B

Z35533

Alloy 2

Zamak 2

AC 43A

Z35545

ZA-8

ZA-8

 ...

Z35638

ZA-12

ZA-12

 ...

Z35633

ZA-27

ZA-27

 ...

Z35841

A See Table 1, Footnote C.
B SAE Specification, Nos. 903 and 925 conform to the requirements for alloys AG40A and AC41A, respectively.
TABLE 1 Chemical Requirements

Element

Alloy 3A,B,C,D
Zamak 3
(AG40A)

Alloy 7A ,B,C,D,E
Zamak 7
(AG40B)

Alloy 5A,B,C,D
Zamak 5
(AC41A)

Alloy 2A,C,,D
Zamak 2
(AC43A)

ZA-8A,C,F
ZA-8

ZA-12A,C ,F
ZA-12

ZA-27A,C,F
ZA-27

 

(Z33525)

(Z33527)

(Z35533)

(Z35545)

(Z35638)

(Z35633)

(Z35841)

Aluminum

3.7-4.3

3.7-4.3

3.7-4.3

3.7-4.3

8.0-8.8

10.5-11.5

25.0-28.0

Magnesium

0.02-0.06G

0.005-0.020

0.02-0.06G

0.02-0.06

0.01-0.03

0.01-0.03

0.01-0.02

Copper

0.1 maxH

0.1 maxE

0.7-1.2

2.6-3.3

0.8-1.3

0.5-1.2

2.0-2.5

Iron, max

0.05

0.05

0.05

0.05

0.075

0.075

0.075

Lead, max

0.005

0.003

0.005

0.005

0.006

0.006

0.006

Cadmium, max

0.004

0.002

0.004

0.004

0.006

0.006

0.006

Tin, max

0.002

0.001

0.002

0.002

0.003

0.003

0.003

Nickel

. . .

0.005-0.020

. . .

. . .

. . .

. . .

. . .

ZincI

remainder

remainder

remainder

remainder

remainder

remainder

remainder

A For purposes of acceptance and rejection, the observed value or calculated value obtained from analysis should be rounded to the nearest unit in the last right-hand place of figures, used in expressing the specified limit, in accordance with the rounding procedure prescribed in Practice E29.
B Zinc alloy castings may contain nickel, chromium, silicon, and manganese in amounts of 0.02, 0.02, 0.035, and 0.06 %, respectively. No harmful effects have ever been noted due to the presence of these elements in these concentrations and, therefore, analyses are not required for these elements, with the exception of nickel analysis for Z33527.
C ASTM alloy designations were established in accordance with Practice B275. The UNS designations were established in accordance with Practice E527. The last digit of a UNS number differentiates between alloys of similar composition. The UNS designations for ingot and casting versions of an alloy were not assigned in the same sequence for all alloys.
D When this material is required to conform to ISO 301, the chemical limits for thallium and indium each shall not exceed 0.001 %.
E For the majority of commercial applications, a copper content up to 0.25 % will not adversely affect the serviceability of these die castings and should not serve as a basis for rejection, unless otherwise specified in the contract or purchase order between the producer and user.
F Zinc-aluminum ingot for foundry and pressure die casting may contain chrome, manganese, or nickel in amounts of up to 0.01 % each or 0.03 % total. No harmful effects have ever been noted due to the presence of these elements in up to these concentrations and, therefore, analyses are not required for these elements.
G Magnesium may be as low as 0.015 % provided that the lead, cadmium, and tin do not exceed 0.003, 0.003, and 0.001 %, respectively.
H For the majority of commercial applications, a copper content of up to 0.7 % will not adversely affect the serviceability of die castings and should not serve as a basis for rejection, unless otherwise specified in the contract or purchase order between the producer and user, such as to meet the requirements of ISO 15201.
I Determined arithmetically by difference.

1.2 Zinc Alloys Z33525, Z33527, Z35533, and Z35545 are used primarily in the manufacture of pressure die castings. Zinc-Aluminum Alloys Z35638, Z35633, and Z35841 are used in the manufacture of both foundry and pressure die castings. These alloys are also fabricated into continuous cast bar stock used for prototyping and screw machine stock.

1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.4 Systems of nomenclature used to designate zinc and zinc-aluminum (ZA) alloys used for casting are described in Appendix X1.

1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

Price:
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Book of Standards Volume: 02.04
Developed by Subcommittee: B02.04
Pages: 7
DOI: 10.1520/B0086-13
ICS Code: 77.150.60