Impact of Calcined Natural Clinoptilolite Zeolite on Hydration Kinetics and Shrinkage of Cementitious Materials

CODEN: ACEMF9

Abstract

Previous literature has provided contradictory results, so we present the current investigation to provide additional information to assess the suitability of using soak calcination as a pretreatment method to increase the performance of calcined zeolite when used as the supplementary cementitious material. In this study, natural clinoptilolite zeolite was calcined for three hours at 200°C, 400°C, 600°C, 800°C, and 1,000°C, and the effects of calcination on different physical and chemical properties were observed using a range of experimental tests. The impacts of calcined zeolite were investigated in the hydrated system with the replacement of portland cement up to 20 % by mass on hydration kinetics (i.e., heat of hydration, setting time, chemical shrinkage, degree of hydration), drying shrinkage, and compressive strength. Results revealed that calcination minorly decreased the crystallinity, particle size, and peak pore size of the zeolite, leading to a slightly increased external specific surface area, whereas it increased the rate of moisture absorption and pH of zeolite particles. In the hydrated cementitious system, calcined zeolite reduced the workability and heat of hydration and retarded the initial setting time. The calcined zeolite particles absorbed a part of the water from the fresh mixture and expanded volumetrically, which led to a negative volume of chemical shrinkage up to the final setting time and increased the drying shrinkage. As the dosages of calcined zeolite increased, the compressive strength substantially decreased because of the lower degree of hydration. Overall, soak calcination pretreatment decreased the reactivity of clinoptilolite zeolite particles and impacted the performance of calcined zeolite in the blended system.

Author Information

Islam, M. Shariful
Department of Civil and Environmental Engineering, Tennessee Tech University, Cookeville, TN, USA
Mohr, Benjamin J.
Department of Civil and Environmental Engineering, Tennessee Tech University, Cookeville, TN, USA
Pages: 33
Price: $25.00
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Stock #: ACEM20220119
ISSN: 2379-1357
DOI: 10.1520/ACEM20220119