This specification covers quenched and tempered vacuum-treated carbon and alloy steel forgings for pressure vessels, such as those used in reactor systems, specifically, vessel closures, shells, flanges, tube sheets, rings, heads, and similar parts. Steels shall be manufactured by basic electric-furnace process except when secondary ladle refining or remelting process is employed, and shall be vacuum treated prior to or during the pouring of the ingot. Materials shall also go through preliminary heat treatment and quenching for mechanical properties. Heat and product analyses shall be executed to evaluate the conformance of the forgings with specified chemical requirements. Tension and Charpy impact tests shall also be performed to examine the conformance of steel specimens with the following mechanical properties: tensile strength, yield strength, elongation, and reduction of area. Nondestructive inspection procedures, such as magnetic particle examination, and longitudinal wave and angle beam ultrasonic examination, shall also be carried out. Repair welding may be permitted at the option of the purchaser.
1.1 This specification covers quenched and tempered vacuum treated carbon and alloy steel forgings for pressure vessels such as those used in reactor systems. Specifically, it covers forgings for vessel closures, shells, flanges, tube sheets, rings, heads, and similar parts.
1.2 All grades are considered weldable under proper conditions. Welding technique is of fundamental importance, and it is presupposed that welding procedure and inspection will be in accordance with approved methods for the grade of material used.
1.3 The values stated in either inch-pound units or SI (metric) units are to be regarded separately as standards. Within the text and the tables, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independent of the other. Combining values from the two systems may result in nonconformance with the specification.
1.4 Unless the order specifies the applicable "M" specification designation, the material shall be furnished to the inch-pound units.
Note 1—Grades 1 and 1A are composed of different chemistries but have the same mechanical requirements.