ASTM A239-14

Standard Practice for Locating the Thinnest Spot in a Zinc (Galvanized) Coating on Iron or Steel Articles,

Standard Practice for Locating the Thinnest Spot in a Zinc (Galvanized) Coating on Iron or Steel Articles, A0239-14 ASTM|A0239-14|en-US Standard Practice for Locating the Thinnest Spot in a Zinc (Galvanized) Coating on Iron or Steel Articles, Standard new BOS Vol. 01.06 Committee A05
$ 73.00 In stock

Significance and Use

2.1 This practice is designed to locate the thinnest portions of the zinc coating on newly coated items (see Appendix X1). Variations in coating thickness can be due to the process by which the zinc is applied (hot dipped, electroplated, or sprayed) or by the geometry of the part that is coated. During hot-dip galvanizing, the coating thickness is affected by the drainage pattern of the molten zinc, while during zinc spraying (metallizing), coating thickness can be dependent on the operator's manipulation of the spray nozzle. The geometry of the part can also influence coating thickness especially during hot-dip galvanizing, where peaks and valleys on the part can cause molten zinc to build up or thin out. This practice is designed to identify those areas of the part where the coating is thin.

Scope

1.1 This practice covers the procedure for locating, by the use of a solution of copper sulfate, the thinnest spot in a zinc coating (hot dipped, electroplated, or sprayed) on iron or steel articles that are coated after the shape is produced by casting, drawing, pressing, or other forming methods. Examples are: electrical metallic tubing and rigid conduit pipe, castings and forgings, and structural steel; on special hardware, such as poleline, builder's, and farm implement hardware; bolts, nuts, screws, and other miscellaneous general hardware.

1.2 The use of this practice with zinc coating deposited through different processes (such as hot dipped, electroplated, or sprayed) requires caution in interpretation since the end point may vary considerably between different zinc-coating systems.

1.3 Excluded from this practice is sheet steel from hot-dip or electrocoating lines as the sheet products are normally subject to additional forming after the coating process. Also excluded from this practice are all zinc-coated wire and wire products either continuously or batch coated before or after forming. Warning—Past research (dating from around 1963) has indicated that this practice can be influenced by operator technique. Variations can be due to the difference in hand pressure used to wipe the sample or the inability of the operator to recognize the end point.

1.4 This technique removes the zinc coating on the surface of the part being examined. This coating removal makes the part or article unusable after testing. This technique may not be suitable for parts fabricated into their final configuration, since they will not be acceptable after testing.

1.5 The results of this practice should not be used to predict the service life of the galvanized coating. Other factors such as location of the thinnest spot, orientation of the part in service, and specific environmental conditions will also affect the service life.

1.6 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Price:
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Book of Standards Volume: 01.06
Developed by Subcommittee: A05.07
Pages: 4
DOI: 10.1520/A0239-14
ICS Code: 25.220.40