    ASTM F21 - 20

    Стандартный метод испытания для определения гидрофобных пленок с использованием распылителя

    Active Standard ASTM F21 Developed by Subcommittee: E21.05

    Book of Standards Volume: 15.03


      Format Pages Price  
    PDF 8 $97.00   ADD TO CART

    Historical Version(s) - view previous versions of standard

    Translated Standard(s): English

    ASTM License Agreement

    More E21.05 Standards Related Products


    Significance and Use

    5.1 The atomizer test as described in this test method is rapid, nondestructive, and may be used for control and evaluation of processes for the removal of hydrophobic contaminants. The test may also be used for the detection and control of hydrophobic contaminants in processing environments. For this application, a surface free of hydrophobic films is exposed to the environment and subsequently tested.4

    5.2 This test method is related to Test Method F22. This test method may be suitable as an alternative to the water-break test when the surface of interest should not or cannot be immersed or doused with water, or when such immersion or dousing is impractical.

    Note 1: This test method is not appropriate where line of sight evaluation is not feasible; or for assembled hardware where there is a risk for entrapment of water in faying surfaces or complex structures where it may not be effectively removed.

    5.3 This test method is not quantitative and is typically restricted to applications where a pass/fail evaluation of cleanliness will suffice.

    5.4 For quantitative measurement of surface wetting, test methods that measure contact angle of a sessile drop of water or other test liquid may be used in some applications. Measurement methods based on contact angle are shown in Test Methods C813, D5946, and D7490; and Practice D7334.

    5.4.1 Devices for in situ measurement of contact angle are available. These devices are limited to a small measurement surface area and may not reflect the cleanliness condition of a larger surface. For larger surface areas, localized contact angle measurement, or other quantitative inspection, combined with water break testing may be useful.

    5.5 This test method is only for use on test surfaces composed of materials, such as metal surfaces, that are hydrophilic (“wettable”) when clean. Some materials such as gold and many plastics are poorly wetted by water, making contamination difficult to detect by this method.

    1. Область применения

    1.1 Данный метод испытания рассматривает определение присутствия гидрофобных (водоотталкивающих) пленок на поверхностях, а также определяет присутствие гидрофобных органических материалов при работе со средой. Если данное испытание проводится надлежащим образом, оно позволяет определить наличие неполного молекулярного слоя гидрофобных органических примесей. При работе с очень грубыми пористыми поверхностями точность испытания может значительно снизиться.

    1.2 Единицы измерения — Значения, указанные в единицах СИ, должны рассматриваться в качестве стандартных. Значения, приведенные в скобках после единиц СИ, представлены исключительно для информации и не должны рассматриваться в качестве стандартных.

    1.3 Настоящий стандарт не ставит целью описание всех проблем безопасности, если они имеются, связанных с его использованием. В обязанности пользователя настоящего стандарта входит определение надлежащих методов техники безопасности, охраны труда и окружающей среды, а также определение применимости нормативных ограничений перед его использованием.

    1.4 Настоящий международный стандарт был разработан в соответствии с признанными на международном уровне принципами стандартизации, установленными в Решении о принципах разработки международных стандартов, руководств и рекомендаций, выпущенном Всемирной торговой организацией, Комитетом по техническим барьерам в торговле (TBT).

    2. Ссылочные документы