    ASTM D6290 - 19

    Стандартный метод испытания для определения цвета пластмассовых гранул

    Active Standard ASTM D6290 Developed by Subcommittee: D20.40

    Book of Standards Volume: 08.03


      Format Pages Price  
    PDF 9 $200.00   ADD TO CART

    Historical Version(s) - view previous versions of standard

    Translated Standard(s): English

    ASTM License Agreement

    More D20.40 Standards Related Products


    Significance and Use

    4.1 Before proceeding with this test method, refer to the specification of the material being tested. Any test specimen preparation, conditioning, dimensions, or testing parameters, or a combination thereof, covered in the materials specification shall take precedence over those mentioned in this test method. If there are no material specifications, then default conditions apply.

    Note 2: Some materials, such as polyamide (nylon), can be cooled very differently during the production of the pellets. This variation in the cooling of the pellets can result in different levels of crystallinity in the pellets only. More crystalline nylons will be more opaque than amorphous nylons. This will result in differences in pellet opacity. The pellet shape is independent of the crystallinity of the material. This variation in pellet appearance, due to varying levels of crystallinity, does not affect final properties.

    Note 3: This test method should not be used for general material specifications.

    4.2 This test method describes a technique useful for making color comparisons of resins in pellet form that is fast and convenient as it does not require preparation, such as molding or extruding specimens. The test method shall be used only to compare specimens of similar pellet shape, size, texture, and degree of translucency. For example, compare translucent disc-shaped pellets to translucent disc-shaped pellets, not with opaque, rectangular shaped pellets.

    4.3 Exact measurements of resin pellet color are not necessarily directly related to the color of the final cast, molded or extruded product due to the multitude of variables, such as producing variables, methods, and pellet shape and size. Color measurements can be useful for comparing resins in pellet form when all samples are similar in shape and size.

    4.4 A three-number tristimulus system is necessary to quantify color completely and precisely. The general method used in this procedure measures color using the CIE Systems described in Practice E308, Test Method D2244, the CIE 1976 (X, Y, Z) system, and, the CIELAB 1976 color space.3

    4.5 Individual components of the tristimulus measurement such as CIE Y (Luminance), Hunter L, a, b, or CIE L*, a*, b* values or other useful metrics like yellowness index in accordance with Practice E313 can be used to describe color attributes of materials.

    1. Область применения

    1.1 Настоящий метод испытания используется для инструментального измерения степени желтизны (или изменения степени желтизны) в условиях дневного освещения однородных, не флуоресцирующих, почти бесцветных прозрачных или почти белых полупрозрачных или непрозрачных пластмасс. Измерение проводится на гранулах и основано на координатах цвета, полученных с помощью спектрофотометра или колориметра.

    1.2 Данный метод испытания применим к цветовому анализу пластмассовых гранул. Возможно, что каждый материал обладает уникальными характеристиками, которые определяют значения цвета.

    1.3 Данная процедура описывает метод определения цветовых измерений, таких как показатель желтизны Index (YI), CIE X, Y, Z и система Хантера L, a, b или CIE L*, a*, b*.

    1.4 Значения, указанные в единицах СИ, должны рассматриваться в качестве стандартных. Значения, приведенные в скобках, представлены исключительно для информации.

    1.5 Настоящий стандарт не ставит целью описание всех проблем безопасности, если они имеются, связанных с его использованием. В обязанности пользователя настоящего стандарта входит определение надлежащих методов техники безопасности и охраны труда, а также определение применимости нормативных ограничений перед его использованием.

    ПРИМЕЧАНИЕ 1 — Данный стандарт и стандарт ISO 17223 относятся к одному и тому же предмету, но различаются по техническомусодержанию.

    1.6 Настоящий международный стандарт разработан в соответствии с международно признанными принципами стандартизации, установленными в Решении о принципах разработки международных стандартов, руководств и рекомендаций Комитета по техническим барьерам в торговле (TBT) Всемирной торговой организации.