    ASTM D2578 - 17

    Стандартный метод испытаний натяжения при смачивании полиэтиленовых и полипропиленовых пленок

    Active Standard ASTM D2578 Developed by Subcommittee: D20.19

    Book of Standards Volume: 08.01


      Format Pages Price  
    PDF 6 $97.00   ADD TO CART

    Historical Version(s) - view previous versions of standard

    Translated Standard(s): English

    ASTM License Agreement

    More D20.19 Standards Related Products


    Significance and Use

    4.1 When a drop of liquid rests on the surface of a solid, and a gas is in contact with both, the forces acting at the interfaces must balance. These forces can be represented by surface energies acting in the direction of the surfaces and it follows that:

    Equation D2578-17_1

    where:

    θ   =   angle of contact of the edge of the drop with the solid surface,
    γGL   =   surface energy of the gas - liquid interface,
    γGS   =   surface energy of the gas - solid interface, and
    γSL   =   surface energy of the solid - liquid interface.

    4.1.1 The right side of the above equation (the difference between the surface energies of the gas - solid and solid - liquid interfaces) is defined as the wetting tension of the solid surface. It is not a fundamental property of the surface but depends on interaction between the solid and a particular environment.

    4.1.2 When the gas is air saturated with vapors of the liquid, γGL will be the surface tension of the liquid. If the angle of contact is 0° the liquid is said to just wet the surface of the solid, and in this particular case (since cos θ = 1) the wetting tension of the solid will be equal to the surface tension of the liquid.

    4.2 The ability of polyethylene and polypropylene films to retain inks, coatings, adhesives, etc., is primarily dependent upon the character of their surfaces, and can be improved by one of several surface-treating techniques. These same treating techniques have been found to increase the wetting tension of a polyethylene or a polypropylene film surface in contact with mixtures of formamide and ethyl Cellosolve in the presence of air. It is therefore possible to relate the wetting tension of a polyethylene or a polypropylene film surface to its ability to accept and retain inks, coatings, adhesives, etc. The measured wetting tension of a specific film surface can only be related to acceptable ink, coating, or adhesive retention through experience. Wetting tension in itself is not a completely acceptable measure of ink, coating, or adhesive adhesion.

    Note 3: A wetting tension of 35 dynes/cm or higher has been generally found to reveal a degree of treatment normally regarded as acceptable for tubular film made from Type 1 polyethylene and intended for commercial flexographic printing. It is, however, possible that some other level of wetting tension may be required to indicate the acceptability of polyethylene films made by other processes, or from other types of polyethylene, or intended for other uses.

    At the present date, insufficient experience has been gained to state a generally acceptable level of wetting tension for polypropylene films for commercial flexographic printing.

    1. Область применения

    1.1 Настоящий метод испытаний охватывает измерение натяжения при смачивании поверхности полиэтиленовой или полипропиленовой пленки, контактирующей с каплями конкретных испытательных растворов в присутствии воздуха.

    1.2 Значения, указанные в единицах СИ, должны рассматриваться в качестве стандартных. Значения,приведенные в скобках, являются математическими преобразованиями в единицы измерения дюйм-фунт, которые приведены только для информации и не считаются стандартными.

    ПРИМЕЧАНИЕ 1 — Данный метод испытаний и указанные реактивыбыли специально разработаны для полиэтиленовых и полипропиленовых пленок. Настоящий метод испытаний и указанные реактивы можно использовать для пленок, состоящих из других полимеров, но это может повлиять на поверхностные энергии границраздела газ-жидкость и твердое тело-жидкость, что повлияет на угол контакта и натяжение при смачивании. Применимость и актуальность использования неполиолефиновых материалов должны быть установлены пользователем.

    1.3 Настоящий стандарт не ставит целью описание всех проблем безопасности, если они имеются, связанных с его использованием. В обязанности пользователя настоящего стандарта входит определение надлежащих методов техники безопасности и охраны труда, а также определение применимости нормативных ограничений перед его использованием. Конкретные сведения об источникахопасности приведены в разделе 8.

    ПРИМЕЧАНИЕ 2 — Настоящий метод испытаний аналогичен стандарту ISO 8296.

    1.4 Настоящий международный стандарт был разработан в соответствии с признанными на международном уровне принципами стандартизации, установленными в Решении о принципах разработки международных стандартов, руководств и рекомендаций, выпущенном Всемирной торговой организацией, Комитетом по техническим барьерам в торговле (TBT).

    2. Ссылочные документы