ASTM D1894 - 14

    Стандартный метод определения статического и кинетического коэффициентов трения для пленок и листовых покрытий из пластмассы

    Active Standard ASTM D1894 Developed by Subcommittee: D20.19

    Book of Standards Volume: 08.01

      Format Pages Price  
    PDF 22 $97.00   ADD TO CART

    Historical Version(s) - view previous versions of standard

    Translated Standard(s): English

    ASTM License Agreement

    More D20.19 Standards Related Products

    Significance and Use

    4.1 Measurements of frictional properties may be made on a film or sheeting specimen when sliding over itself or over another substance. The coefficients of friction are related to the slip properties of plastic films that are of wide interest in packaging applications. These methods yield empirical data for control purposes in film production. Correlation of test results with actual performance can usually be established.

    4.1.1 This test method includes testing at temperatures other than 23°C by heating only the plane while the sled is at ambient temperature.

    4.2 Slip properties are generated by additives in some plastic films, for example, polyethylene. These additives have varying degrees of compatibility with the film matrix. Some of them bloom, or exude to the surface, lubricating it and making it more slippery. Because this blooming action may not always be uniform on all areas of the film surface, values from these tests may be limited in reproducibility.

    4.3 The frictional properties of plastic film and sheeting may be dependent on the uniformity of the rate of motion between the two surfaces. Care should be exercised to ensure that the rate of motion of the equipment is as carefully controlled as possible.

    4.4 Data obtained by these procedures may be extremely sensitive to the age of the film or sheet and the condition of the surfaces. The blooming action of many slip additives is time-dependent. For this reason, it is sometimes meaningless to compare slip and friction properties of films or sheets produced at different times, unless it is desired to study this effect.

    4.5 Frictional and slip properties of plastic film and sheeting are based on measurements of surface phenomena. Where products have been made by different processes, or even on different machines by the same process, their surfaces may be dependent on the equipment or its running conditions. Such factors must be weighed in evaluating data from these methods.

    4.6 The measurement of the static coefficient of friction is highly dependent on the rate of loading and on the amount of blocking occurring between the loaded sled and the platform due to variation in time before motion is initiated.

    4.7 Care should be exercised to make certain that the speed of response of the recorder, either electronic or mechanical, is not exceeded.

    4.8 For many materials, there may be a specification that requires the use of this test method, but with some procedural modifications that take precedence when adhering to the specification. Therefore, it is advisable to refer to that material specification before using this test method. Table 1 of Classification System D4000 lists the ASTM materials standards that currently exist.

    1. Область применения

    1.1Данный метод испытаний охватывает определение коэффициентов начального периода трения и трения скольжения пленки и листов из пластмассы при скольжении по собственной поверхности или по поверхности других веществ в заданных условиях испытания. Методика допускает применение неподвижных салазок и подвижной плоскости или подвижных салазок и неподвижной плоскости. Обе методики дают одинаковые значения коэффициентов трения для данной пробы. ПРИМЕЧАНИЕ1 — Для характеристик трения пластмассовых пленок частично обернутых вокруг цилиндра или барабана см. Метод испытаний G 143, находящийся под юрисдикцией Подкомитета ASTM G02.50.

    1.2 Данные, полученные настоящим методом испытаний, релевантны и пригодны для применения в техническом проектировании.

    1.2.1Как вариант данного испытания коэффициент трения можно получить при температурах, отличных от 23 С, путем нагревания только плоскости, оставляя салазки при окружающей температуре.

    1.3Значения, указанные в единицах СИ, считаются стандартными. Значения в скобках приведены только для информации.

    1.4 Данный стандарт не претендует на полноту описания всех мер безопасности, если таковые имеются, связанных с его использованием. Вся ответственность за установление соответствующих правил техники безопасности и мер по охране здоровья, а также определение пределов применимости регламентов до начала использования данного стандарта, лежит на пользователе стандарта. Специальные положения по технике безопасности см. в конце 6.5.

    ПРИМЕЧАНИЕ 2 — Данный метод испытаний не идентичен ISO 8295-1995, и нельзя непосредственно сравнивать результаты двух методов.

    2. Ссылочные документы