ASTM D1003 - 13

    Стандартные методы определения мутности и коэффициента пропускания света прозрачных пластмасс

    Active Standard ASTM D1003 Developed by Subcommittee: D20.40

    Book of Standards Volume: 08.01


      Format Pages Price  
    PDF 23 $97.00   ADD TO CART

    Historical Version(s) - view previous versions of standard

    Translated Standard(s): English

    ASTM License Agreement

    More D20.40 Standards Related Products


    Significance and Use

    4.1 Light that is scattered upon passing through a film or sheet of a material can produce a hazy or smoky field when objects are viewed through the material. Another effect can be veiling glare, as occurs in an automobile windshield when driving into the sun.

    4.2 Although haze measurements are made most commonly by the use of a hazemeter, a spectrophotometer may be used, provided that it meets the geometric and spectral requirements of Section 5. The use of a spectrophotometer for haze measurement of plastics can provide valuable diagnostic data on the origin of the haze,4 and Procedure B is devoted to the use of a spectrophotometer.

    4.2.1 Procedure A (hazemeter) test values are normally slightly higher and less variable than Procedure B (spectrophotometer) test values.

    4.3 Regular luminous transmittance is obtained by placing a clear specimen at some distance from the entrance port of the integrating sphere. However, when the specimen is hazy, the total hemispherical luminous transmittance must be measured by placing the specimen at the entrance port of the sphere. The measured total hemispherical luminous transmittance will be greater than the regular luminous transmittance, depending on the optical properties of the sample. With this test method, the specimen is necessarily placed at the entrance port of the sphere in order to measure haze and total hemispherical luminous transmittance.

    4.4 Haze data representative of the material may be obtained by avoiding heterogeneous surface or internal defects not characteristic of the material.

    4.5 Haze and luminous-transmittance data are especially useful for quality control and specification purposes.

    4.6 Before proceeding with this test method, reference should be made to the specification of the material being tested. Any test specimen preparation, conditioning, dimensions, or testing parameters, or combination thereof, covered in the materials specification shall take precedence over those mentioned in this test method. If there are no material specifications, then the default conditions apply.

    1. Область применения

    1.1 Настоящий метод испытаний относится к определению специфических свойств пропускания и широкоугольного рассеяния света для плоских профилей таких материалов, как очень прозрачные пластмассы. Для измерения коэффициента пропускания света (прозрачности) и мутности предусмотрены две процедуры. В Процедуре А используется мутномер, как описано в разделе 5, а в Процедуре В используется спектрофотометр, как описано в разделе 8. Материал, имеющий значение мутности более 30%, считается светорассеивающим, и его следует испытывать согласно Методике Е 2387.

    1.2 Значения, указанные в единицах СИ, должны рассматриваться как стандартные.

    ПРИМЕЧАНИЕ 1 ― Для большего различения материалов, которые рассеивают высокий процент света в пределах узкого угла рассеяния вперед, таких как истертые прозрачные пластмассы, настраивают мутномер и проводят измерение согласно Методу испытаний D 1044.

    1.3 Данный стандарт не претендует на полноту описания всех мер безопасности, если таковые имеются, связанных с его использованием. Вся ответственность за установление соответствующих правил техники безопасности и мер по охране здоровья, а также определение пределов применимости регламентов до начала использования данного стандарта, лежит на пользователе стандарта.

    ПРИМЕЧАНИЕ 2 ― Данный метод испытаний не являются технически эквивалентным ISO 13468-1 и ISO/DIS 14782.

    2. Ссылочные документы