    ASTM D1002 - 10(2019)

    Стандартный метод определения прочности на сдвиг склеенных внахлест металлических образцов под действием разрывающей нагрузки (металл-металл)

    Active Standard ASTM D1002 Developed by Subcommittee: D14.80

    Book of Standards Volume: 15.06


      Format Pages Price  
    PDF 8 $200.00   ADD TO CART

    Historical Version(s) - view previous versions of standard

    Translated Standard(s): English

    ASTM License Agreement

    More D14.80 Standards Related Products


    Significance and Use

    4.1 This test method is primarily comparative. However, it does have application as a discriminator in determining variations in adherend surface preparation parameters and adhesive environmental durability. The test method has found applications in controlling surface preparations, primer, and adhesive systems for determining strength properties of tested systems.

    4.2 The misuse of strength values obtained from this test method as design-allowable stress values for structural joints could lead to product failure, property damage, and human injury. The apparent shear strength of an adhesive obtained from a given small single-lap specimen may differ from that obtained from a joint made with different adherends or by a different bonding process. The normal variation of temperature and moisture in the service environment causes the adherends and the adhesive to swell or shrink. The adherends and adhesive are likely to have different thermal and moisture coefficients of expansion.

    4.3 Even in small specimens, short-term environmental changes may induce internal stresses or chemical changes in the adhesive that permanently affect the apparent strength and other mechanical properties of the adhesive. The problem of predicting joint behavior in a changing environment is even more difficult if a different type of adherend is used in a larger structural joint than was used in the small specimen.

    4.4 The apparent shear strength measured with a single-lap specimen is not suitable for determining design-allowable stresses for designing structural joints that differ in any manner from the joints tested without thorough analysis and understanding of the joint and adhesive behaviors.

    4.5 Single-lap tests may be used for comparing and selecting adhesives or bonding processes for susceptibility to fatigue and environmental changes, but such comparisons must be made with great caution since different adhesives may respond differently in different joints. See Guide D4896 for further discussion of the concepts relative to interpretation of adhesive-bonded single-lap-joints.

    1. Область применения

    1.1 Этот метод испытаний охватывает определение прочности на сдвиг клеев для склеивания металлов при испытании на стандартном склеенном внахлест металлическом образце и при определенных условиях подготовки и испытания.

    1.2 Значения, указанные в единицах СИ, должны рассматриваться в качестве стандартных. Значения, приведенные в скобках после единиц измерения СИ, представляются исключительно в информационных целях и недолжны рассматриваться в качестве стандартных.

    1.3 Настоящий стандарт не ставит целью описание всех проблем безопасности, если они имеются, связанных с его использованием. В обязанности пользователя настоящего стандарта входит определение надлежащих методов техники безопасности и охраны труда и окружающей среды, а также определение применимости нормативных ограничений перед его использованием.

    1.4 Настоящий международный стандарт был разработан в соответствии с признанными на международном уровне принципами стандартизации, установленными в Решении о принципах разработки международных стандартов, руководств и рекомендаций, выпущенном Всемирной торговойорганизацией, Комитетом по техническим барьерам в торговле (TBT).