Effects of Multiple Shot-Peening/Cadmium-Plating Cycles on High-Strength Steel

Source

A study was made of the effects of multiple shot-peening and cadmium plating operations on high-strength AISI 4340 steel used in aircraft landing-gear applications. No detrimental effects were observed on surface microstructure and tensile properties or on fatigue and unnotched stress corrosion resistance in high-humidity air. An apparent degradation in stress corrosion life of fatigue precracked specimens was observed after four and five peening and plating operations.

Author Information

Kohls, JB
Metcut Research Associates Inc., Cincinnati, Ohio
Cammett, JT
Metcut Research Associates Inc., Cincinnati, Ohio
Gunderson, AW
U.S. Air Force, AFWAL/MLLX, Wright-Patterson Air Force Base, Ohio
Price: $25.00
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Developed by Committee: E08
Pages: 158–171
DOI: 10.1520/STP30103S
ISBN-EB: 978-0-8031-4841-3
ISBN-13: 978-0-8031-0711-3