    Volume 11, Issue 2 (April 2021)

    Special Issue Paper

    Corrosion Behavior of Surface Nanostructured IN718 Superalloy at 650°C

    (Received 20 October 2020; accepted 1 February 2021)

    Published Online: 07 April 2021

    CODEN: MPCACD

      Format Pages Price  
    PDF (4.74 MB) 14 $25   ADD TO CART

    Cite this document

    X Add email address send
    X
      .RIS For RefWorks, EndNote, ProCite, Reference Manager, Zoteo, and many others.   .DOCX For Microsoft Word



    Abstract

    In the present study, the process of ultrasonic shot peening (USP) was adopted for developing nanostructures with a grain size of 62 ± 10 nm on the surface of the alloy IN718. The effect of nanostructures was investigated on high-temperature corrosion behavior under cyclic exposure at 650°C for 100 h in different salty environments (weight percent): 100NaCl (T1), 75Na2SO4 + 25NaCl (T2), and 90Na2SO4 + 5NaCl + 5V2O5 (T3). A near parabolic rate law was observed in both non-treated and treated conditions; however, the parabolic rate constant (kp) was reduced for the USP-treated specimens coated with Salt T1 and Salt Mixtures T2 and T3 by nearly 41 %, 52 %, and 50 %, respectively, with respect to the non-treated specimens. Several oxides and spinels such as TiO2, Fe2O3, Fe3O4, Cr2O3, FeVO4, NbO2, NiFe2O4, NiCr2O4, NiVO3, FeNbO4, FeCr2O4, Na2Cr2O7, and Cr2(MoO4)3 and sulfides NiS and FeS and chlorides CrCl3 and NiCl2 were observed in both treated as well as non-treated samples.

    Author Information:

    Kumar, Sanjeev
    DRDO Defence Metallurgical Research Laboratory, DMRL Hyderabad Kanchanbagh, Hyderabad, Telangana

    Chattopadhyay, K.
    Department of Metallurgical Engineering, Indian Institute of Technology (Banaras Hindu University), Varanasi, Uttar Pradesh

    Alam, Z.
    DRDO Defence Metallurgical Research Laboratory, DMRL Hyderabad Kanchanbagh, Hyderabad, Telangana

    Singh, Vakil
    Department of Metallurgical Engineering, Indian Institute of Technology (Banaras Hindu University), Varanasi, Uttar Pradesh

    Satyanarayana, D. V. V.
    DRDO Defence Metallurgical Research Laboratory, DMRL Hyderabad Kanchanbagh, Hyderabad, Telangana

    Kumar, Vikas
    DRDO Defence Metallurgical Research Laboratory, DMRL Hyderabad Kanchanbagh, Hyderabad, Telangana


    Stock #: MPC20200156

    ISSN:2379-1365

    DOI: 10.1520/MPC20200156

    Author
    Title Corrosion Behavior of Surface Nanostructured IN718 Superalloy at 650°C
    Symposium ,
    Committee D18