ASTM G39-99

    Standard Practice for Preparation and Use of Bent-Beam Stress-Corrosion Test Specimens

      Format Pages Price  
    PDF 7 $55.20   ADD TO CART

    1. Scope

    1.1 This practice covers procedures for designing, preparing, and using bent-beam stress-corrosion specimens.

    1.2 Different specimen configurations are given for use with different product forms, such as sheet or plate. This practice applicable to specimens of any metal that are stressed to levels less than the elastic limit of the material, and therefore the applied stress can be accurately calculated or measured (Note 1). Stress calculations by this practice are not applicable to plastically stressed specimens.

    Note 1-It is the nature of these methods that only the applied stress can be calculated. Since stress-corrosion cracking is a function of the total stress, for critical applications and proper interpretation of results, the residual stress (before applying external stress) or the total elastic stress (after applying external stress) should be determined by appropriate nondestructive methods, such as X-ray diffraction (1).

    1.3 Test procedures are given for stress-corrosion testing by exposure to gaseous and liquid environments.

    1.4 The bent-beam test is best suited for flat product forms such as sheet, strip, and plate. For plate material the bent-beam specimen is more difficult to use, because more rugged specimen holders must be built to accommodate the specimens. A double-beam modification of a four-point specimen to utilize heavier materials is described in 10.5.

    1.5 The exposure of specimens in a corrosive environment is treated only briefly, since other methods deal with this aspect, for example, Specification D1141, Practices G30, G36, G44, and G50, and Method G43. The experimenter is referred to ASTM Special Technical Publication 425 (2).

    1.6 The bent-beam method generally constitutes a constant strain (deflection) test. Once cracking has initiated, the state of stress at the tip of the crack as well as in uncracked areas has changed, and therefore the known or calculated stress or strain values discussed in this method apply only to the state of stress existing before initiation of cracks.

    1.7 The values stated in SI units are to be regarded as standard. The inch-pound equivalents in parentheses are provided for information.

    1.8 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. (For more specific safety hazard information see Section 8 and 12.1.)

    2. Referenced Documents (purchase separately) The documents listed below are referenced within the subject standard but are not provided as part of the standard.

    ASTM Standards

    D1141 Practice for the Preparation of Substitute Ocean Water

    G30 Practice for Making and Using U-Bend Stress-Corrosion Test Specimens

    G36 Practice for Evaluating Stress-Corrosion-Cracking Resistance of Metals and Alloys in a Boiling Magnesium Chloride Solution

    G44 Practice for Exposure of Metals and Alloys by Alternate Immersion in Neutral 3.5 % Sodium Chloride Solution

    G50 Practice for Conducting Atmospheric Corrosion Tests on Metals

    G85 Practice for Modified Salt Spray (Fog) Testing

    NACE Documents

    NACE TM0177-96 Laboratory Testing of Metals for Resistance to Specific Forms of Environmental Cracking in H2S Environments

    ICS Code

    ICS Number Code 77.040.10 (Mechanical testing of metals); 77.060 (Corrosion of metals)

    UNSPSC Code

    UNSPSC Code

    Referencing This Standard
    Link Here
    Link to Active (This link will always route to the current Active version of the standard.)

    DOI: 10.1520/G0039-99

    Citation Format

    ASTM G39-99, Standard Practice for Preparation and Use of Bent-Beam Stress-Corrosion Test Specimens, ASTM International, West Conshohocken, PA, 1999,

    Back to Top