1.1 This specification covers ten types of portland cement, as follows (see ):
1.1.1 Type I—For use when the special properties specified for any other type are not required.
1.1.2 Type IA—Air-entraining cement for the same uses as Type I, where air-entrainment is desired.
1.1.3 Type II—For general use, more especially when moderate sulfate resistance is desired.
1.1.4 Type IIA—Air-entraining cement for the same uses as Type II, where air-entrainment is desired.
1.1.5 Type II(MH)—For general use, more especially when moderate heat of hydration and moderate sulfate resistance are desired.
1.1.6 Type II(MH)A—Air-entraining cement for the same uses as Type II(MH), where air-entrainment is desired.
1.1.7 Type III—For use when high early strength is desired.
1.1.8 Type IIIA—Air-entraining cement for the same use as Type III, where air-entrainment is desired.
1.1.9 Type IV—For use when a low heat of hydration is desired.
1.1.10 Type V—For use when high sulfate resistance is desired.
Note 1: Some cements are designated with a combined type classification, such as Type I/II, indicating that the cement meets the requirements of the indicated types and is being offered as suitable for use when either type is desired.
Note 2: Cement conforming to the requirements for all types are not carried in stock in some areas. In advance of specifying the use of cement other than Type I, determine whether the proposed type of cement is, or can be made, available.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. Values in SI units [or inch-pound units] shall be obtained by measurement in SI units [or inch-pound units] or by appropriate conversion, using the Rules for Conversion and Rounding given in , of measurements made in other units [or SI units]. Values are stated in only SI units when inch-pound units are not used in practice.
1.3 The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents (purchase separately) The documents listed below are referenced within the subject standard but are not provided as part of the standard.
C51 Terminology Relating to Lime and Limestone (as used by the Industry)
C109/C109M Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)
C114 Test Methods for Chemical Analysis of Hydraulic Cement
C151/C151M Test Method for Autoclave Expansion of Hydraulic Cement
C185 Test Method for Air Content of Hydraulic Cement Mortar
C191 Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle
C204 Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus
C219 Terminology Relating to Hydraulic and Other Inorganic Cements
C226 Specification for Air-Entraining Additions for Use in the Manufacture of Air-Entraining Hydraulic Cement
C266 Test Method for Time of Setting of Hydraulic-Cement Paste by Gillmore Needles
C451 Test Method for Early Stiffening of Hydraulic Cement (Paste Method)
C452 Test Method for Potential Expansion of Portland-Cement Mortars Exposed to Sulfate
C465 Specification for Processing Additions for Use in the Manufacture of Hydraulic Cements
C563 Guide for Approximation of Optimum SO3 in Hydraulic Cement
C1038/C1038M Test Method for Expansion of Hydraulic Cement Mortar Bars Stored in Water
C1702 Test Method for Measurement of Heat of Hydration of Hydraulic Cementitious Materials Using Isothermal Conduction Calorimetry
C1778 Guide for Reducing the Risk of Deleterious Alkali-Aggregate Reaction in Concrete
E29 Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications
ICS Number Code 91.100.10 (Cement. Gypsum. Lime. Mortar)
UNSPSC Code 30111601(Cement)
|Link to Active (This link will always route to the current Active version of the standard.)|
ASTM C150 / C150M-17, Standard Specification for Portland Cement, ASTM International, West Conshohocken, PA, 2017, www.astm.orgBack to Top