STP907

    Composite Materials: Fatigue and Fracture

    Thomas Hahn H

    Pages: 397

    Published: 1986

    Purchase Print    $122

    Purchase Print + PDF    $183.00
       Save 25%    more info



    The symposium on Composite Materials: Fatigue and Fracture was held in Dallas, Texas, 24-25 October 1984. ASTM Committee D30 on High Modulus Fibers and Their Composites sponsored the symposium. H. Thomas Hahn, Washington University, presided as symposium chairman and editor of this publication.


    Table of Contents

    Introduction
    Hahn H.

    Summary
    Hahn H.

    Dynamic Delamination Crack Propagation in a Graphite/Epoxy Laminate
    Grady J., Sun C.

    Influence of Mold Coverage upon the Notch Strength of R25 Sheet Molding Compounds
    Onachuk M., Shirrell C.

    Interface Studies of Aluminum Metal Matrix Composites
    Fu L., Marcus H., Schmerling M.

    Probabilistic Fracture Kinetics of “Natural” Composites
    Krausz A., Krausz K., Necsulescu D.

    Constrained 90-Deg Ply Cracking in 0/90/0 and ±45/90/∓45 CFRP Laminates
    Peters P.

    Fracture of Thick Graphite/Epoxy Laminates with Part-Through Surface Flaws
    Harris C., Morris D.

    Failure Analysis of a Graphite/Epoxy Laminate Subjected to Bolt-Bearing Loads
    Crews J., Naik R.

    Damage Mechanics Analysis of Matrix Effects in Notched Laminates
    Aronsson C., Bäcklund J.

    Fatigue Behavior of Continuous-Fiber Silicon Carbide/Aluminum Composites
    Johnson W., Wallis R.

    Delamination Arrester—An Adhesive Inner Layer in Laminated Composites
    Chan W.

    Fatigue Damage in Notched Pultruded Composite Rods
    Little R., Mallick P., Thomas J.

    Fatigue Failure Mechanisms in Unidirectional Composites
    Hahn H., Lorenzo L.

    Internal Load Distribution Effects During Fatigue Loading of Composite Laminates
    Highsmith A., Reifsnider K.

    On the Interrelationship Between Fiber Fracture and Ply Cracking in Graphite/Epoxy Laminates
    Jamison R.

    Damage Mechanisms and Accumulation in Graphite/Epoxy Laminates
    Charewicz A., Daniel I.

    A Critical-Element Model of the Residual Strength and Life of Fatigue-Loaded Composite Coupons
    Reifsnider K., Stinchcomb W.

    Response of Thick, Notched Laminates Subjected to Tension-Compression Cyclic Loads
    Bakis C., Stinchcomb W.

    Effect of Ply Thickness on Longitudinal Splitting and Delamination in Graphite/Epoxy Under Compressive Cyclic Load
    Lagace P., Nolet S.

    Influence of Sublaminate Cracks on the Tension Fatigue Behavior of a Graphite/Epoxy Laminate
    Carlsson L., Eidefeldt C., Mohlin T.

    Author Index

    Subject Index


    Committee: D30

    Paper ID: STP907-EB

    DOI: 10.1520/STP907-EB

    ISBN-EB: 978-0-8031-4973-1

    ISBN-PRINT: 978-0-8031-0470-9

    ASTM International is a member of CrossRef.

    0-8031-0470-7
    978-0-8031-0470-9
    STP907-EB