    Corrosion of Metals Under Thermal Insulation

    Pollock WI, Barnhart JM
    Published: 1985


      Format Pages Price  
    PDF (6.9M) $73   ADD TO CART
    Hardcopy (shipping and handling) $73   ADD TO CART
    Hardcopy + PDF Bundle - Save 25%
    (shipping and handling)
    $109.50   ADD TO CART


    Provides the latest information on the serious corrosion problems that can occur to thermally insulated plant equipment, tankcage and piping components if the insulation becomes wet and reviews the various control and inspection methods being used and under development

    Table of Contents

    Introduction
    Pollock W.

    The Function of Thermal Insulation
    Barnhart J.

    Factors Affecting Corrosion of Carbon Steel Under Thermal Insulation
    Lazar P.

    Factors Affecting the Stress Corrosion Cracking of Austenitic Stainless Steels Under Thermal Insulation
    McIntyre D.

    A Review of the European Meeting on Corrosion Under Lagging Held in England, November 1980
    Richardson J.

    Thermal Insulation Materials: Generic Types and Their Properties
    Lang G.

    Experience with Corrosion Beneath Thermal Insulation in a Petrochemical Plant
    Sandberg T.

    Recent Experiences with Corrosion Beneath Thermal Insulation in a Chemical Plant
    Crawley P., Long V.

    Failure of Type 316 Stainless Steel Nozzles in Contact with Fire Retardant Mastic
    Moniz B., Ritter M.

    External Stress Corrosion Cracking of Stainless Steel Under Thermal Insulation—20 Years Later
    Ashbaugh W.

    Shell and Jacket Corrosion of a Foamed In-Place Thermally Insulated Liquefied Petroleum Gas Tank
    Bennett R., Taylor D.

    A Study of Corrosion of Steel Under a Variety of Thermal Insulation Materials
    Ashbaugh W., Laundrie T.

    Behavior of a Copper Water Tube Exposed to Natural Carbonaceous Granular and Cellulosic Insulation Materials
    Cohen A., Myers J.

    Controlling Carbon Steel Corrosion Under Insulation
    Krystow P.

    Protective Coating System Design for Insulated or Fireproofed Structures
    Collins P., Delahunt J., Maatsch D.

    Prevention of Chloride Stress Corrosion Cracking Under Insulation
    Sumbry L., Vegdahl E.

    Designing to Prevent Corrosion of Metals Under Insulation
    Mettam C.

    Use of Aluminum Foil for Prevention of Stress Corrosion Cracking of Austenitic Stainless Steel Under Thermal Insulation
    Fitzsimmons T., Richardson J.

    Using Specifications to Avoid Chloride Stress Corrosion Cracking
    Kalis J.

    Use Inspection as a Means of Reducing Failures Caused By Corrosion Under Wet Insulation
    Moak H.

    A New Apparatus and Test Procedure for Running ASTM C 692 Stress Corrosion Cracking Tests
    Hutto F., Tissot R., Whitaker T.

    Comparisons of Several Accelerated Corrosiveness Test Methods for Thermal Insulating Materials
    Patel S., Sheppard K., Taneja M., Weil R.

    Author Index

    Subject Index


    Committee: C16

    Paper ID: STP880-EB

    DOI: 10.1520/STP880-EB

    ISBN-EB: 978-0-8031-5591-6