STP513

    Stress Analysis and Growth of Cracks: Proceedings of the 1971 National Symposium on Fracture Mechanics: Part 1

    Corten HT, Gallagher JP
    Published: 1972


      Format Pages Price  
    PDF Version (4.6M) $94   ADD TO CART
    Print Version $94   ADD TO CART
    Print + PDF Bundle - Save 25% $141.00   ADD TO CART


    The 1971 National Symposium on Fracture Mechanics was held at the University of Illinois, Urbana-Champaign, Ill., 31 August through 2 September 1971. H.T. Corten, Department of Theoretical and Applied Mechanics, University of Illinois, presided as general chairman. J.P. Gallagher, Experimental Mechanics Branch, Air Force Flight Dynamics Laboratory, Wright-Patterson AFB, served as arrangements chairman.


    Table of Contents

    Introduction

    Stress Intensity Factor for an Elliptical Crack Approaching the Surface of a Plate in Bending
    Kobayashi A., Shah R.

    A Study of Local Stresses Near Surface Flaws in Bending Fields
    Marrs G., Smith C.

    Stress Intensity Factors for Surface Cracks in Bending
    Grandt A., Sinclair G.

    Stress Intensity Factors for Internally Pressurized Thick-Wall Cylinders
    Underwood J.

    Crack Shapes and Stress Intensity Factors for Edge-Cracked Specimens
    Orange T.

    Toward Assessing the Effects of Crack Front Curvature (CFC)
    Ritter M., Swedlow J.

    Some Crack Tip Finite Elements for Plane Elasticity
    Wilson W.

    Fatigue Crack Growth Data for Various Materials Deduced from the Fatigue Lives of Precracked Plates
    Pook L.

    Fatigue Threshold Crack Propagation in Air and Dry Argon for a Ti-6Al-4V Alloy
    Anderson A., Bucci R., Hertzberg R., Paris P., Schmidt R.

    Extensive Study of Low Fatigue Crack Growth Rates in A533 and A508 Steels
    Bucci R., Clark W., Mager T., Paris P., Wessel E.

    Fatigue Crack Propagation Growth Rates under a Wide Variation of ΔK for an ASTM A517 Grade F (T-1) Steel
    Bucci R., Clark W., Paris P.

    Fatigue Crack Propagation of D6ac Steel in Air and Distilled Water
    Bucci R., Little C., Paris P.

    The Effect of Frequency upon the Fatigue-Crack Growth of Type 304 Stainless Steel at 1000 F
    James L.

    Delay Effects in Fatigue Crack Propagation
    Hertzberg R., Roberts R., von Euw E.

    Fatigue Crack Growth Analysis of Pressurized Water Reactor Vessels
    Mager T., Riccardella P.

    Rayleigh Waves for Continuous Monitoring of a Propagating Crack Front
    Buck O., Ho C., Marcus H., Thompson R.

    Fracture Mechanics Consideration of Hydrogen Sulfide Cracking in High Strength Steels
    Bucci R., Johnson H., Loushin L., Paris P.


    Committee: E08

    Paper ID: STP513-EB

    DOI: 10.1520/STP513-EB

    ISBN-EB: 978-0-8031-4615-0

    ISBN-13: 978-0-8031-0362-7

    ASTM International is a member of CrossRef.

    0-8031-0362-X
    978-0-8031-0362-7
    STP513-EB