Stress-Corrosion Cracking of Titanium
Pages: 270
Published: 1966
|
|
Table of Contents
Elevated-Temperature Static and Dynamic Sea-Salt Stress Cracking of Titanium Alloys
Avery C., Turley R.
The Relative Stress-Corrosion Susceptibility of Titanium Alloys in the Presence of Hot Salt
Fager D., Piper D.
Environmental Effects Studies on Selected Titanium Alloys
Orden J., Simenz R., Wald G.
The Mechanism of Salt Attack on Titanium Alloys
Bomberger H., Petersen V.
Investigation of Long-Term Exposure Effects Under Stress of Two Titanium Structural Alloys
Martin G.
Effects of Environment on Cracking in Titanium Alloys
Erbin E., Hatch A., Rosenberg H.
Basic Mechanisms of Stress-Corrosion Cracking of Titanium
Louthan M., Rideout S., Selby C.
An Investigation of Stress-Corrosion Failures in Titanium Compressor Components
Antony K., Duttweiler R., Wagner R.
Effects of Salt Atmosphere on Crack Sensitivity of Commercial Titanium Alloys at 600 to 900 F
Danesi W., Donachie M., Pinkowish A.
Salt Stress Corrosion of Ti-8Al-1Mo-1V Alloy Sheet at Elevated Temperatures
Braski D., Dexter H., Heimerl G., Royster D.
Chemical and Physical Mechanisms of Salt Stress-Corrosion Cracking in the Titanium 8-1-1 Alloy
Bechtoldt C., Logan H., McBee M., Sanderson B., Ugiansky G.
The Diffusion of Corrosion Products in Hot-Salt Stress-Corrosion Cracking of Titanium
Kirchner R., Ripling E.
Sea-Water Embrittlement of Titanium
Cavallaro J., Lane I., Morton A.