STP1110

    Composite Materials: Fatigue and Fracture (Third Volume)

    O'Brien TK

    Pages: 826

    Published: 1991

    Purchase PDF (20M)    $163

    Purchase Print    $163

    Purchase Print + PDF    $244.50
       Save 25%    more info



    38 papers by authors from universities, government, and industry give a balanced presentation on these subjects:

    • Matrix Cracking and Delamination

    • Interlaminar Fracture Toughness

    • Delamination Analysis

    • Strength and Impact

    • Fatigue and Fracture.

    For aircraft designers, researchers in aerospace materials, composite material manufacturers, aerospace professors; also engineering designers, engineering professors.


    Table of Contents

    Overview
    O'Brien T.

    Fracture Mechanics Approaches to Transverse Ply Cracking in Composite Laminates
    Boniface L., Ogin S., Smith P.

    Matrix Cracking in Composite Laminates with Resin-Rich Interlaminar Layers
    Dost E., Grande D., Ilcewicz L., McCool J.

    The Upper Bounds of Reduced Axial and Shear Moduli in Cross-Ply Laminates with Matrix Cracks
    Allen D., Harris C., Lee J.

    Cooling Rate Effects in Carbon Fiber/PEEK Composites
    Cantwell W., Davies P., Jar P., Kausch H., Neville D., Richard H.

    Effects of Moisture Absorption on Edge Delamination, Part I: Analysis of the Effects of Nonuniform Moisture Distributions on Strain Energy Release Rate
    Hooper S., Subramanian R., Toubia R.

    Effects of Moisture Absorption on Edge Delamination, Part II: An Experimental Study of Jet Fuel Absorption on Graphite-Epoxy
    Hooper S., Subramanian R., Toubia R.

    Effect of Porosity on Flange-Web Corner Strength
    Bhatia N., Kan H., Mahler M.

    Mixed-Mode Fracture in Fiber-Polymer Composite Laminates
    Hashemi S., Kinloch A., Williams G.

    Effects of T-Tabs and Large Deflections in Double Cantilever Beam Specimen Tests
    Crews J., Naik R., Shivakumar K.

    Experimental Determination of the Mode I Behavior of a Delamination Under Mixed-Mode Loading
    Chinatambi N., Poursartip A.

    Stabilized End Notched Flexure Test: Characterization of Mode II Interlaminar Crack Growth
    Kageyama K., Kikuchi M., Yanagisawa N.

    Initiation and Growth of Mode II Delamination in Toughened Composites
    Russell A.

    Evaluation of the Split Cantilever Beam for Mode III Delamination Testing
    Martin R.

    Fracture Analysis of Transverse Crack-Tip and Free-Edge Delamination in Laminated Composites
    Armanios E., Badir A., Sriram P.

    Combined Effect of Matrix Cracking and Free Edge on Delamination
    O'Brien T., Salpekar S.

    Fatigue Delamination Onset Prediction in Unidirectional Tapered Laminates
    Murri G., O'Brien T., Salpekar S.

    Delamination Analysis of Tapered Laminated Composites Under Tensile Loading
    Armanios E., Parnas L.

    Analysis of Delamination Growth in Compressively Loaded Composite Laminates
    Tratt M.

    A Study of an Implanted Delamination Within a Cylindrical Composite Panel
    Palazotto A., Wilder B.

    A Comparison of Experimental Observations and Numerical Predictions for the Initiation of Fiber Microbuckling in Notched Composite Laminates
    Bradley W., Guynn E., Ochoa O., Whitcomb J.

    Three-Dimensional Stress Analysis of Plain Weave Composites
    Whitcomb J.

    Compression Testing of Thick-Section Composite Materials
    Camponeschi E.

    Influence of Low-Velocity Impact on Composite Structures
    Madan R.

    Effects of Stacking Sequence on Impact Damage Resistance and Residual Strength for Quasi-Isotropic Laminates
    Avery W., Coxon B., Dost E., Ilcewicz L.

    Relevance of Impacter Shape to Nonvisible Damage and Residual Tensile Strength of a Thick Graphite/Epoxy Laminate
    Poe C.

    Response of Composite Plates to Quasi-Static Impact Events
    Bucinell R., Koury J., Nuismer R.

    Compression of Composite Materials: A Review
    Camponeschi E.

    Fatigue Behavior of Continuous Carbon Fiber-Reinforced PEEK
    Curtis D., Davies M., Moore D., Slater B.

    Damage-Based Notched Strength Modeling: A Summary
    Beaumont P., Kortschot M.

    Fatigue Damage Mechanics of Notched Graphite-Epoxy Laminates
    Ashby M., Beaumont P., Spearing M.

    Hole Effect and Compression Fatigue of T300/N5208 Composite Materials
    Bathias C., Lai D.

    Effect of Interlaminar Normal Stresses on the Uniaxial Zero-to-Tension Fatigue Behavior of Graphite/Epoxy Tubes
    An D., Krempl E.

    Effects of Notch Geometry and Moisture on Fracture Strength of Carbon/Epoxy and Carbon/Bismaleimide Laminates
    Bandyopadhyay S., Burch I., Underwood J.

    Fatigue Failure Processes in Aligned Carbon-Epoxy Laminates
    Lam P., Piggott M.

    Fracture of Fibrous Metal Matrix Composites Containing Discontinuities
    Bahei-El-Din Y.

    Fatigue Crack Growth in a Unidirectional SCS-6/Ti-15-3 Composite
    Ghosn L., Kantzos P., Telesman J.

    Thermomechanical Fatigue of a Quasi-Isotropic Metal Matrix Composite
    Majumdar B., Newaz G.

    Observations of Fatigue Crack Initiation and Damage Growth in Notched Titanium Matrix Composites
    Johnson W., Naik R.

    Damage and Performance Characterization of ARALL Laminates Subjected to Tensile Cyclic Loading
    Osiroff R., Reifsnider K., Stinchcomb W.

    Effective Crack Lengths by Compliance Measurement for ARALL-2 Laminates
    Wilson C., Wilson D.

    An Investigation of the Effects of Temperature on the Impact Behavior and Residual Tensile Strength of an ARamid Aluminum Laminate (ARALL-2 Laminate)
    Lee T., Wilson D.

    Author Index

    Subject Index


    Committee: D30

    Paper ID: STP1110-EB

    DOI: 10.1520/STP1110-EB

    ISBN-EB: 978-0-8031-5169-7

    ISBN-PRINT: 978-0-8031-1419-7

    ASTM International is a member of CrossRef.

    0-8031-1419-2
    978-0-8031-1419-7
    STP1110-EB