STP1153

    Stress and Thermal Analysis of Resistance Temperature Detectors

    Published: Jan 1994


      Format Pages Price  
    PDF Version (296K) 14 $25   ADD TO CART
    Complete Source PDF (4.2M) 14 $55   ADD TO CART


    Abstract

    In many industries the failure of temperature devices such as resistance temperature detectors (RTDs) are of significance to process control. Therefore, a study was instituted to evaluate these failures. RTDs from various manufacturers were monitored and periodically calibrated until failure. Sensors that developed open circuits were then examined. Upon examination of the sensors, it was found that failures were occurring at or near the solder connection between the platinum lead-out and copper wire. A two-dimensional (2-D) finite element analysis of this joint was then developed.

    Finite element models were created to evaluate stresses at 100, 200, and 300°C. The thermal expansion mismatch between the wires joined by the solder results in high-stress gradients at the corners of the solder joint. Photomicrographs were produced of the joint failures with a scanning electron microscope to study the crack nucleation and propagation. Aging of the solder due to long-term temperature exposure may also play a key role in the fracture behavior. The need for improved joint design and special coating materials is of primary importance to improve the life of the solder joints in many applications. This will improve the reliability of the components.

    Keywords:

    electronic materials, finite-element-analysis, solder joint, fracture, high temperature, resistance temperature detectors, platinum wire, copper wire, thermal stresses


    Author Information:

    Wilson, DA
    Professor.and graduate student, Tennessee Technological University, Cookeville, TN

    Katherisan, A
    Professor.and graduate student, Tennessee Technological University, Cookeville, TN


    Paper ID: STP23921S

    Committee/Subcommittee: E08.05

    DOI: 10.1520/STP23921S


    CrossRef ASTM International is a member of CrossRef.