    Crack Growth Resistance of Laser Surface Remelted Nodular Cast Iron

    Published: Apr 2012


      Format Pages Price  
    PDF Version (656K) 16 $25   ADD TO CART
    Complete Source PDF (30M) 16 $139   ADD TO CART


    Abstract

    The laser surface remelting (LSR) process is applied to modify the surface properties of nodular cast iron and is suitable for manufacture of various machine and tool parts. Usually, studies of surface remelted layers include microstructural and microchemical analyses, measurements of residual stresses, and various wear and corrosion tests. This paper will represent microstructural and microhardness analyses of the thin surface layer after laser remelting of nodular cast iron 500-7. Particular attention is paid to fatigue crack initiation and propagation tests. Crack initiation and growth behavior was assessed under bending test conditions. The comparison is made between as-received nodular cast iron 500-7 and the same material, where one of the surfaces is altered with the LSR process. As the crack propagation is perpendicular to the laser remelted layer, the specimens with a thin laser surface remelted layer exhibited higher resistance to fatigue crack growth in the low stress intensity factor range ΔKth than as-received nodular cast iron specimens. Also, ΔKIC is higher in the case of the laser remelted surface.

    Keywords:

    laser surface remelting, nodular cast iron, residual stresses, fatigue, crack growth resistance


    Author Information:

    Šturm, Roman
    Faculty of Mechanical Engineering, Univ. of Ljubljana, Ljubljana,

    Grum, Janez
    Faculty of Mechanical Engineering, Univ. of Ljubljana, Ljubljana,


    Paper ID: STP153220120038

    Committee/Subcommittee: D02.L0

    DOI: 10.1520/STP153220120038


    CrossRef ASTM International is a member of CrossRef.