    Mechanical Properties of Four 7–9%Cr Reduced Activation Martensitic Steels after 2.5 dpa, 300°C Irradiation

    Published: Jan 2000


      Format Pages Price  
    PDF (296K) 14 $25   ADD TO CART
    Complete Source PDF (27M) 14 $371   ADD TO CART


    Abstract

    Reduced Activation Ferritic/Martensitic alloys are being developed for application in future thermonuclear fusion reactors. The behavior of the reduced activation martensitic steel F82H-mod was compared with small amounts of related alloys JLF-1, JLF-1B and ORNL-9Cr2WVTa, following irradiation in the High Flux Reactor (HFR) in Petten. Tensile, KLST-type Charpy impact and CT fracture toughness mechanical properties specimens, were neutron irradiated to a dose level of 2–3 dpa at 300°C. Results of post irradiation tensile, miniaturized charpy impact, and static fracture toughness tests are presented and interpreted in terms of irradiation hardening and irradiation induced shift of ductile to brittle transition temperature (DBTT) and reduction of upper shelf energy (USE). The observed irradiation hardening (140 – 170 MPa at 300°C) is moderate, whereas the observed radiation induced shift in DBTT is approximately 150°C for KLST-type impact test specimens for F82H. Similar observations are made for the static fracture toughness tests. For JLF-1B the irradiation hardening is one third higher than for JLF-1, and shift in DBTT for JLF-1B is almost 70% larger than for JLF-1. The difference is attributed to the tenfold larger boron content prior to irradiation.

    Keywords:

    neutron irradiation, ferritic-martensitic 7–9%Cr steels, low activation, tensile properties, fracture toughness, Charpy impact behavior, embrittlement, hardening, ductility


    Author Information:

    van Osch, E
    Materials scientists, NRG (former ECN), ZG Petten,

    Horsten, M
    Materials scientists, NRG (former ECN), ZG Petten,

    Lucas, GE
    Professor, University of California Santa Barbara, Santa Barbara, CA

    Odette, GR
    Professor, University of California Santa Barbara, Santa Barbara, CA


    Paper ID: STP12418S

    Committee/Subcommittee: E10.08

    DOI: 10.1520/STP12418S


    CrossRef ASTM International is a member of CrossRef.