    The Analysis of Fretting Fatigue Failure in Backup Roll and its Prevention

    Published: Jan 2003


      Format Pages Price  
    PDF Version (348K) 12 $25   ADD TO CART
    Complete Source PDF (11M) 12 $215   ADD TO CART


    Abstract

    In the present research, a fretting fatigue failure in a backup roll (BUR) was examined. Fretting fatigue properties of the roll material were experimentally obtained and the prevention of the fretting fatigue failure was proposed. BUR is one of the most important components in a steel making rolling mill for the control of plate thickness and flatness. The BUR was initially supported by oil film bearings. Recently, oil film bearings have been rapidly replaced by roller bearings for the purpose of high-precision rolling. After the replacements, fretting fatigue failures of BUR have begun to occur. Rotating bending fatigue tests were performed with a 40 mm diameter shrink-fit axle to evaluate the fretting fatigue strength of the BUR material and to examine the improvement of the fretting fatigue strength of the holding part of the BUR. The effects of roller machining and overhanging of the contact edge on the fretting fatigue strength were investigated. Based on the results of this study, roller machining was applied to the holding part of the BUR. Furthermore, the diameter of the holding part of the BUR was increased. No failure occurred due to fretting in the BUR for more than four years since these countermeasures were applied.

    Keywords:

    fretting fatigue, failure analysis, steel making rolling mill, backup roll, shrink-fitted axle, surface rolling, overhanging of the contact edge


    Author Information:

    Kubota, M
    Technical Assistant, Kyushu University, Fukuoka,

    Odanaka, H
    Graduate School of Kyushu University,

    Sakae, C
    Associate Professor, Kyushu University,

    Ohkomori, Y
    Japan Casting & Forging Corp., Kitakyushu,

    Kondo, Y
    Professor, Kyushu University,


    Paper ID: STP10775S

    Committee/Subcommittee: E08.01

    DOI: 10.1520/STP10775S


    CrossRef ASTM International is a member of CrossRef.