Influence of Non-Metallic Inclusions on the Fracture-Toughness Properties on the Longitudinal Welding of an API 5L Steel Pipeline

CODEN: JTEVAB

Abstract

In previous works, it was demonstrated that the average fracture-toughness values were higher in the circumferential-longitudinal direction (CL) than in the circumferential-radial direction (CR) on the longitudinal submerged arc welding (SAW) in API 5L pipeline steel. Nevertheless, such differences in fracture-toughness values were attributed to the density distribution of microstructural phases and porosity, but the effect of non-metallic inclusions on this fracture property was not considered; therefore, the present work analyzed the effect of non-metallic inclusions on the fracture-toughness values by fractographic and electron diffraction scattered analyses. The results showed the presence of titanium (Ti), calcium (Ca), and aluminum (Al) constituents in the non-metallic inclusions for the CR direction of the pipeline. These elements tended to form compounds that promoted brittle-fracture by cleavage, decreasing the toughness properties of the weld. For the CL direction analysis, the elements presented on the non-metallic inclusions were manganese (Mn), silicon (Si), and sulfur (S), which promoted the nucleation and coalescence of cavities, all of which were typical for ductile fracture. Calculations on the KIC showed that the non-metallic inclusions with elements of Ti, Ca, and Al contributed to lower KIC values on the CR direction under analysis.

Author Information

Angeles-Herrera, D.
Instituto Mexicano del Petróleo, México, D.F., C.P., US
Albiter-Hernández, A.
Instituto Mexicano del Petróleo, México, D.F., C.P., US
Cuamatzi-Meléndez, R.
Instituto Mexicano del Petróleo, México, D.F., C.P., US
Morales-Ramirez, A.
Instituto Politécnico Nacional, México, D.F., C.P., US
Pages: 8
Price: $25.00
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Stock #: JTE20150061
ISSN: 0090-3973
DOI: 10.1520/JTE20150061