    Prediction of the Shape of the KJ Ductile-to-Brittle Transition Temperature Curve for Ferritic Pressure Vessel Steels Using the Material's Resistance to Crack Extension KJ versus Δa Curve

    CODEN: JAIOAD

      Format Pages Price  
    PDF 10 $25   ADD TO CART


    Abstract

    Fracture toughness (KJ (cleavage)) measurements made within the ductile-to-brittle transition region for ferritic pressure vessel steels are not always described by the shape of the Master Curve currently given in ASTM Standard E 1921. The objective of this paper is to show how the shape of the transition toughness curve may be related to the shape of the material's resistance to crack extension curve (KJR) once the crack tip starts to blunt and ductile crack extension precedes cleavage failure. Using an empirical relationship between the mean ductile crack extension (Δa) prior to the onset of cleavage failure and temperature (Δa=λ exp(ϕT)), then the relationship between KJ and T may simply be given by KJ=KA+α[λ exp(ϕT)]β, where KA, α, and β are simply the coefficients to an offset power law to KJ versus Δa data given by KJR=KA+α(Δa)β. For specimens of different sizes, a reference temperature TK may be defined for a given reference level of Δa or equivalent KJ. Unique curves may be defined for materials with differing crack extension resistance curves through plots of KJ versus (T−TΔa(ref)) or (T−TK(ref)). The generalized form of the transition curve may be given by KJ=KA+α{Δa(ref) exp[ϕ(T−TΔa(ref))]}β or KJ=KA+(K(ref)KA){exp[ϕ(T−TK(ref))]}β. Experimentally, ϕ has been estimated as approximately 0.08 for nuclear pressure vessel materials such as A533B/A508. Using a specific situation wherein the value of KA=30MPam,K(ref)=100MPam, and β=0.25 then, for a B=25-mm specimen, within experimental scatter this provides an almost exact match to the Master Curve given by KJ=30+70 exp[0.019(T−TK100)]. The predictions of transition curve shape using the material's resistance to crack extension curve are believed to be complementary to the Master Curve method, and may describe the shape of the transition curve when there is ductile crack extension prior to cleavage failure. Further work is recommended to investigate the relationship between the predicted ductile-to-brittle transition curve and the Master Curve for probabilities of cleavage failure post-initiation.


    Author Information:

    Wardle, G
    Technical Director, Warhelle Consulting Ltd, Lowton, Cheshire

    Geary, W
    Section Head (Metallurgy & Materials) Health and Safety Laboratory, Buxton,


    Stock #: JAI13208

    ISSN: 1546-962X

    DOI: 10.1520/JAI13208

    ASTM International is a member of CrossRef.

    Author
    Title Prediction of the Shape of the KJ Ductile-to-Brittle Transition Temperature Curve for Ferritic Pressure Vessel Steels Using the Material's Resistance to Crack Extension KJ versus Δa Curve
    Symposium , 0000-00-00
    Committee E08