1. Rationale
Section 5.1 is being revised to include the statement that - fluoride ions have the potential to induce stress corrosion cracking in the absence of inhibiting ions. Section 5.3 is replaced with a more complete and accurate statement as a resolution to previous comments.
Keywords
austenitic stainless steel; chloride; Dana test; Drip test; external stress corrosion cracking (ESCC); qualification test; thermal insulation; wicking insulation; Corrosion--insulating materials; Corrosion--stress-corrosion; Cracking--insulation; External stress corrosion cracking (ESCC); Stainless steel (corrosion testing); Stress corrosion cracking (SCC); Wicking; Austenitic stainless steel thermal insulation;