ASTM G30 - 97(2009) Standard Practice for Making and Using U-Bend Stress-Corrosion Test Specimens


    Citing ASTM Standards Citation data is made available by participants in CrossRefs Cited-by Linking service. A comprehensive list of citations to this standard are listed here.

    C692 Standard Test Method for Evaluating the Influence of Thermal Insulations on External Stress Corrosion Cracking Tendency of Austenitic Stainless Steel

    G4 Standard Guide for Conducting Corrosion Tests in Field Applications

    G35 Standard Practice for Determining the Susceptibility of Stainless Steels and Related Nickel-Chromium-Iron Alloys to Stress-Corrosion Cracking in Polythionic Acids

    G36 Standard Practice for Evaluating Stress-Corrosion-Cracking Resistance of Metals and Alloys in a Boiling Magnesium Chloride Solution

    G37 Standard Practice for Use of Mattsson's Solution of pH 7.2 to Evaluate the Stress- Corrosion Cracking Susceptibility of Copper-Zinc Alloys

    G39 Standard Practice for Preparation and Use of Bent-Beam Stress-Corrosion Test Specimens

    G41 Standard Practice for Determining Cracking Susceptibility of Metals Exposed Under Stress to a Hot Salt Environment

    G52 Standard Practice for Exposing and Evaluating Metals and Alloys in Surface Seawater

    G58 Standard Practice for Preparation of Stress-Corrosion Test Specimens for Weldments

    G103 Standard Practice for Evaluating Stress-Corrosion Cracking Resistance of Low Copper 7XXX Series Al-Zn-Mg-Cu Alloys in Boiling 6% Sodium Chloride Solution

    G111 Standard Guide for Corrosion Tests in High Temperature or High Pressure Environment, or Both

    G123 Standard Test Method for Evaluating Stress-Corrosion Cracking of Stainless Alloys with Different Nickel Content in Boiling Acidified Sodium Chloride Solution

    G157 Standard Guide for Evaluating Corrosion Properties of Wrought Iron- and Nickel-Based Corrosion Resistant Alloys for Chemical Process Industries


    Referenced ASTM Standards The documents listed below are referenced within the subject standard but are not provided as part of the standard.

    E3 Guide for Preparation of Metallographic Specimens

    G1 Practice for Preparing, Cleaning, and Evaluating Corrosion Test Specimens

    G15 Terminology Relating to Corrosion and Corrosion Testing

    G35 Practice for Determining the Susceptibility of Stainless Steels and Related Nickel-Chromium-Iron Alloys to Stress-Corrosion Cracking in Polythionic Acids

    G36 Practice for Evaluating Stress-Corrosion-Cracking Resistance of Metals and Alloys in a Boiling Magnesium Chloride Solution

    G37 Practice for Use of Mattssons Solution of pH 7.2 to Evaluate the Stress-Corrosion Cracking Susceptibility of Copper-Zinc Alloys

    G39 Practice for Preparation and Use of Bent-Beam Stress-Corrosion Test Specimens

    G41 Practice for Determining Cracking Susceptibility of Metals Exposed Under Stress to a Hot Salt Environment

    G44 Practice for Exposure of Metals and Alloys by Alternate Immersion in Neutral 3.5 % Sodium Chloride Solution

    G49 Practice for Preparation and Use of Direct Tension Stress-Corrosion Test Specimens

    G103 Practice for Evaluating Stress-Corrosion Cracking Resistance of Low Copper 7XXX Series Al-Zn-Mg-Cu Alloys in Boiling 6 % Sodium Chloride Solution

    G123 Test Method for Evaluating Stress-Corrosion Cracking of Stainless Alloys with Different Nickel Content in Boiling Acidified Sodium Chloride Solution