SUPERSEDED (click for Active standard)
1.1 This test method describes laboratory procedures for determining the sliding wear of ceramics, metals, and other candidate wear-resistant materials using a linear, reciprocating ball-on-flat plane geometry. The direction of the relative motion between sliding surfaces reverses in a periodic fashion such that the sliding occurs back and forth and in a straight line. The principal quantities of interest are the wear volumes of the contacting ball and flat specimen materials; however, the coefficient of kinetic friction may also be measured using the method described. This test method encompasses both unlubricated and lubricated testing procedures. The scope of this test method does not include testing in corrosive or chemically aggressive environments.
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
2. Referenced Documents (purchase separately) The documents listed below are referenced within the subject standard but are not provided as part of the standard.
E112 Test Methods for Determining Average Grain Size
E1181 Test Methods for Characterizing Duplex Grain Sizes
G40 Terminology Relating to Wear and Erosion
G99 Test Method for Wear Testing with a Pin-on-Disk Apparatus
G115 Guide for Measuring and Reporting Friction Coefficients
G117 Guide for Calculating and Reporting Measures of Precision Using Data from Interlaboratory Wear or Erosion Tests
G118 Guide for Recommended Format of Wear Test Data Suitable for Databases
UNSPSC Code 41114625(Wear testers)
ASTM G133-95, Standard Test Method for Linearly Reciprocating Ball-on-Flat Sliding Wear, ASTM International, West Conshohocken, PA, 1995, www.astm.orgBack to Top