1.1 This specification covers hydraulic cements for both general and special applications. This is a specification giving performance requirements. There are no restrictions on the composition of the cement or its constituents.
1.2 The specification classifies cements by type based on specific requirements for general use, high early strength, resistance to attack by sulfates, and heat of hydration. Optional requirements are provided for the property of low reactivity with alkali-reactive aggregates.
1.3 For properties where values are given in both SI and inch-pound units, the values in SI units are to be regarded as the standard. Values in SI units shall be obtained by measurement in SI units or by appropriate conversion, using the Rules for Conversion and Rounding given in IEEE/ASTM SI 10, of measurements made in other units.
1.4 The text of this standard refers to notes and footnotes that provide explanatory material. These notes and footnotes (excluding those in tables and figures) are not requirements of the standard.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
Note 1—Specification C 150 is a prescription specification for portland cement and Specifications C 595 is a specification for blended hydraulic cement where the products that may be furnished are of restricted nature and proportions and where the products must meet prescriptive requirements as to chemical and physical properties.
2. Referenced Documents (purchase separately) The documents listed below are referenced within the subject standard but are not provided as part of the standard.
C109/C109M Test Method for Compressive Strength of Hydraulic Cement Mortars (Using 2-in. or [50-mm] Cube Specimens)
C114 Test Methods for Chemical Analysis of Hydraulic Cement
C150 Specification for Portland Cement
C151 Test Method for Autoclave Expansion of Hydraulic Cement
C183 Practice for Sampling and the Amount of Testing of Hydraulic Cement
C185 Test Method for Air Content of Hydraulic Cement Mortar
C186 Test Method for Heat of Hydration of Hydraulic Cement
C188 Test Method for Density of Hydraulic Cement
C191 Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle
C204 Test Methods for Fineness of Hydraulic Cement by Air-Permeability Apparatus
C219 Terminology Relating to Hydraulic Cement
C227 Test Method for Potential Alkali Reactivity of Cement-Aggregate Combinations (Mortar-Bar Method)
C359 Test Method for Early Stiffening of Hydraulic Cement (Mortar Method)
C430 Test Method for Fineness of Hydraulic Cement by the 45-m (No. 325) Sieve
C441 Test Method for Effectiveness of Pozzolans or Ground Blast-Furnace Slag in Preventing Excessive Expansion of Concrete Due to the Alkali-Silica Reaction
C451 Test Method for Early Stiffening of Hydraulic Cement (Paste Method)
C595 Specification for Blended Hydraulic Cements
C596 Test Method for Drying Shrinkage of Mortar Containing Hydraulic Cement
C1012 Test Method for Length Change of Hydraulic-Cement Mortars Exposed to a Sulfate Solution
C1038 Test Method for Expansion of Hydraulic Cement Mortar Bars Stored in Water
ICS Number Code 91.100.10 (Cement. Gypsum. Lime. Mortar)
UNSPSC Code 30111601(Cement)
|Link to Active (This link will always route to the current Active version of the standard.)|
ASTM C1157-03, Standard Performance Specification for Hydraulic Cement, ASTM International, West Conshohocken, PA, 2003, www.astm.orgBack to Top