Standard Historical Last Updated: Jul 01, 2013 Track Document
ASTM B862-09

Standard Specification for Titanium and Titanium Alloy Welded Pipe

Standard Specification for Titanium and Titanium Alloy Welded Pipe B0862-09 ASTM|B0862-09|en-US Standard Specification for Titanium and Titanium Alloy Welded Pipe Standard new BOS Vol. 02.04 Committee B10
$ 75.00 In stock

Abstract

This specification covers the requirements for 33 grades of titanium and titanium alloy welded pipe intended for general corrosion resisting and elevated temperature service. Welded pipe shall be made from annealed flat-rolled products by a welding process. Welded pipe may be further reduced by cold working or hot working. Grades 1, 2, 2 H, 7, 7H, 11,13, 14, 16, 16H, 17, 26H, 33, and 37 shall be furnished as welded or annealed. Grades 3, 12, 15, and 34 shall be furnished as annealed. Grade 5, 23, 24, 25, 35 shall be furnished as annealed, or aged. Grade 9, 18, 38 shall be furnished as annealed. Grade 19, 20, 21 shall be furnished as solution treated, or solution treated and aged. The materials shall conform to the required chemical composition for nitrogen, carbon, hydrogen, iron, oxygen, aluminum, vanadium, tin, ruthenium, palladium, cobalt, molybdenum, chromium, nickel, niobium, zirconium, silicon, and titanium. They shall also conform to the required mechanical propetries such as tensile strength, yield strength, and elongation.

Scope

1.1 This specification covers the requirements for 33 grades of titanium and titanium alloy welded pipe intended for general corrosion resisting and elevated temperature service as follows:

1.1.1 Grade 1Unalloyed titanium, low oxygen,

1.1.2 Grade 2Unalloyed titanium, standard oxygen,

1.1.2.1 Grade 2HUnalloyed titanium (Grade 2 with 58 ksi minimum UTS),

1.1.3 Grade 3Unalloyed titanium, medium oxygen,

1.1.4 Grade 5Titanium alloy (6 % aluminum, 4 % vanadium),

1.1.5 Grade 7Unalloyed titanium plus 0.12 to 0.25 % palladium, standard oxygen,

1.1.5.1 Grade 7HUnalloyed titanium plus 0.12 to 0.25 % palladium (Grade 7 with 58 ksi minimum UTS),

1.1.6 Grade 9Titanium alloy (3 % aluminum, 2.5 % vanadium),

1.1.7 Grade 11Unalloyed titanium plus 0.12 to 0.25 % palladium, low oxygen,

1.1.8 Grade 12Titanium alloy (0.3 % molybdenum, 0.8 % nickel),

1.1.9 Grade 13Titanium alloy (0.5 % nickel, 0.05 % ruthenium), low oxygen,

1.1.10 Grade 14Titanium alloy (0.5 % nickel, 0.05 % ruthenium), standard oxygen,

1.1.11 Grade 15Titanium alloy (0.5 % nickel, 0.05 % ruthenium), medium oxygen,

1.1.12 Grade 16Unalloyed titanium plus 0.04 to 0.08 % palladium, standard oxygen,

1.1.12.1 Grade 16HUnalloyed titanium plus 0.04 to 0.08 % palladium (Grade 16 with 58 ksi minimum UTS),

1.1.13 Grade 17Unalloyed titanium plus 0.04 to 0.08 % palladium, low oxygen,

1.1.14 Grade 18Titanium alloy (3 % aluminum, 2.5 % vanadium plus 0.04 to 0.08 % palladium),

1.1.15 Grade 19Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconium, 4 % molybdenum),

1.1.16 Grade 20Titanium alloy (3 % aluminum, 8 % vanadium, 6 % chromium, 4 % zirconium, 4 % molybdenum) plus 0.04 to 0.08 % palladium,

1.1.17 Grade 21Titanium alloy (15 % molybdenum, 3 % aluminum, 2.7 % niobium, 0.25 % silicon),

1.1.18 Grade 23Titanium alloy (6 % aluminum, 4 % vanadium, extra low interstitial, ELI),

1.1.19 Grade 24Titanium alloy (6 % aluminum, 4 % vanadium) plus 0.04 to 0.08 % palladium,

1.1.20 Grade 25Titanium alloy (6 % aluminum, 4 % vanadium) plus 0.3 to 0.8 % nickel and 0.04 to 0.08 % palladium,

1.1.21 Grade 26Unalloyed titanium plus 0.08 to 0.14 % ruthenium,

1.1.21.1 Grade 26HUnalloyed titanium plus 0.08 to 0.14 % ruthenium (Grade 26 with 58 ksi minimum UTS),

1.1.22 Grade 27Unalloyed titanium plus 0.08 to 0.14 % ruthenium,

1.1.23 Grade 28Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.08 to 0.14 % ruthenium,

1.1.24 Grade 29Titanium alloy (6 % aluminum, 4 % vanadium with extra low interstitial elements (ELI)) plus 0.08 to 0.14 % ruthenium,

1.1.25 Grade 33Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),

1.1.26 Grade 34Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),

1.1.27 Grade 35Titanium alloy (4.5 % aluminum, 2 % molybdenum, 1.6 % vanadium, 0.5 % iron, 0.3 % silicon),

1.1.28 Grade 37Titanium alloy (1.5 % aluminum), and

1.1.29 Grade 38Titanium alloy (4 % aluminum, 2.5 % vanadium, 1.5 % iron).

Note 1—H grade material is identical to the corresponding numeric grade (that is, Grade 2H = Grade 2) except for the higher guaranteed minimum UTS, and may always be certified as meeting the requirements of its corresponding numeric grade. Grades 2H, 7H, 16H, and 26H are intended primarily for pressure vessel use.

The H grades were added in response to a user association request based on its study of over 5200 commercial Grade 2, 7, 16, and 26 test reports, where over 99 % met the 58 ksi minimum UTS.

1.2 Pipe 8 in. NPS (nominal pipe size) and larger is most frequently custom made for an order. In such cases, the purchaser carefully should consider the applicability of this specification. Since the pipe is custom made, the purchaser may choose a wall thickness other than those in Table 1 to meet specific operating conditions. The purchaser may also be better served to specify only the portions of this specification that are required to meet the operating conditions (for example, annealing, flattening test, chemistry, properties, etc.).

1.3 Optional supplementary requirements are provided for pipe where a greater degree of testing is desired. These supplementary requirements may be invoked by the purchaser, when desired, by specifying in the order.

1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

TABLE 1 Dimensions of Pipe

Note 1—Schedule sizes conform to ANSI/ASME B 36.19M-1985 (for S sizes) or B 36.10 (for non-S sizes).

Note 2—The decimal thickness listed for the respective pipe sizes represent their nominal wall dimensions.

NPS Desig.Outside Dia.Nominal Wall Thickness
Schedule 5SASchedule 5ASchedule 10SASchedule 10ASchedule 40SSchedule 40Schedule 80SSchedule 80
inmminmminmminmminmminmminmminmminmm
1/80.40510.29xxxx0.0491.240.0491.240.0681.730.0681.730.0952.410.0952.41
¼0.54013.72xxxx0.0651.650.0651.650.0882.240.0882.240.1193.020.1193.02
3/80.67517.15xxxx0.0651.650.0651.650.0912.310.0912.310.1263.200.1263.20
½0.84021.340.0651.650.0651.650.0832.110.0832.110.1092.770.1092.770.1473.730.1473.73
¾1.05026.670.0651.650.0651.650.0832.110.0832.110.1132.870.1132.870.1543.910.1543.91
11.31533.400.0651.650.0651.650.1092.770.1092.770.1333.380.1333.380.1794.550.1794.55
1-¼1.66042.160.0651.650.0651.650.1092.770.1092.770.1403.560.1403.560.1914.850.1914.85
1-½1.90048.260.0651.650.0651.650.1092.770.1092.770.1453.680.1453.680.2005.080.2005.08
22.37560.320.0651.650.0651.650.1092.770.1092.770.1543.910.1543.910.2185.540.2185.54
2-½2.87573.020.0832.110.0832.110.1203.050.1203.050.2035.160.2035.160.2767.010.2767.01
33.50088.900.0832.110.0832.110.1203.050.1203.050.2165.490.2165.490.3007.620.3007.62
3-½4.000101.600.0832.110.0832.110.1203.050.1203.050.2265.740.2265.740.3188.080.3188.08
44.500114.300.0832.110.0832.110.1203.050.1203.050.2376.020.2376.020.3378.560.3378.56
55.563141.300.1092.770.1092.770.1343.400.1343.400.2586.550.2586.550.3759.530.3759.53
66.625168.270.1092.770.1092.770.1343.400.1343.400.2807.110.2807.110.43210.970.43210.97
88.625219.070.1092.770.1092.770.1483.760.1483.760.3228.180.3228.180.50012.700.50012.70
1010.75273.050.1343.400.1343.400.1654.190.1654.190.3659.270.3659.270.50012.700.59415.09
1212.75323.850.1563.960.1563.960.1804.570.1804.570.3759.530.40610.310.50012.700.68817.48
1414.00355.600.1563.960.1563.960.1884.780.2506.35xx0.43811.13xx0.75019.05
1616.00406.400.1654.190.1654.190.1884.780.2506.35xx0.50012.70xx0.84421.44
1818.00457.200.1654.190.1654.190.1884.780.2506.35xx0.56214.27xx0.93823.83
2020.00508.000.1884.780.1884.780.2185.540.2506.35xx0.59415.09xx1.03126.19
2222.00558.800.1884.780.1884.780.2185.540.2506.35xxxxxx1.12528.58
2424.00609.600.2185.540.2185.540.2506.350.2506.35xx0.68817.48xx1.21930.96
2626.00660.40xxxxxx0.3127.92xxxxxxxx
2828.00711.20xxxxxx0.3127.92xxxxxxxx
3030.00762.000.2506.350.2506.350.3127.920.3127.92xxxxxxxx
3232.00812.80xxxxxx0.3127.92xx0.68817.48xxxx
3434.00863.60xxxxxx0.3127.92xx0.68817.48xxxx
3636.00914.40xxxxxx0.3127.92xx0.75019.05xxxx

A Threading not permitted in accordance with ANSI B.1.20.1.

Price:
Contact Sales
Related
Reprints and Permissions
Reprints and copyright permissions can be requested through the
Copyright Clearance Center
Details
Book of Standards Volume: 02.04
Developed by Subcommittee: B10.01
Pages: 9
DOI: 10.1520/B0862-09
ICS Code: 77.150.50