1.1 This practice covers testing and inspection and is applicable to bars, billets, and blooms of carbon, alloy, and stainless steel which have been consumable electrode remelted.
1.2 For the purpose of this practice, the consumable electrode remelting process is defined as a steel refining method wherein single or multiple electrodes are remelted into a crucible producing an ingot which is superior to the original electrode by virtue of improved cleanliness or lower gas content or reduced chemical or nonmetallic segregation. See and for descriptions of applicable remelting processes.
1.3 This practice and the accompanying comparison macrographs are generally applicable to steel bar and billet sizes up to 225 in.2 [1450 cm2] in transverse cross section.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
2. Referenced Documents (purchase separately) The documents listed below are referenced within the subject standard but are not provided as part of the standard.
E381 Method of Macroetch Testing Steel Bars, Billets, Blooms, and Forgings
consumable electrode remelting; electroslag remelting; freckles; macro etching; radial segregation; ring pattern; segregation; vacuum arc remelting; white spots; Alloy steel bars; Electrochemical measurements/testing; Electrode remelted steel; Macroetching; Stainless steel bars/billets; Steel bars; Steel bars and billets